正交实验法优化季戊四溴的制备工艺

玻璃钢/复合材料 ›› 2010, Vol. 210 ›› Issue (1): 67-69.

正交实验法优化季戊四溴的制备工艺

陈少杰¹，张教强¹，蒙宇²

(1.西北工业大学，陕西西安710129；2.西安工业大学，陕西西安710072)

出版日期:2010-01-28 发布日期:2010-01-28
作者简介:陈少杰(1982-)，男，硕士研究生，主要从事应用化学方面的研究。

OPTIMIZATION OF PROCESSING TECHNOLOGY FOR PENTAERYTHRITYL
TETRABROMIDE WITH ORTHOGONAL DESIGN

Online:2010-01-28 Published:2010-01-28

摘要/Abstract

摘要：

以季戊四溴的产率为指标，利用L9（34)正交试验法考察了反应时间、反应温度、催化剂含量对产率的影响。结果表明，最佳制备工艺条件为反应时间为14h，反应温度为140～150℃，催化剂含量为1.5g。其中反应时间对产率有较显著的影响。

关键词: 季戊四溴, 正交实验, 制备工艺, 产率

Abstract:

To optimize the processing technology for pentaerythrityl tetrabromide with yield ratio as a marker，with the method of orthogonal experimental design,the paper investigates the influencing factors such as reaction time，reaction temperature and the content of catalyst. The result shows that the optimum condition of processing technology is reactive for 14 hours，with the temperature of 140~150℃， and the content of catalyst is 1.5g. The reaction time has significant effect on the yield ratio.

Key words: pentaerythrityl tetrabromide, orthogonal design, processing technology, yield ratio

中图分类号:

TQ222.2⁺15

陈少杰, 张教强, 蒙宇. 正交实验法优化季戊四溴的制备工艺[J]. 玻璃钢/复合材料, 2010, 210(1): 67-69.

Chen, S. J., Z. J. J., Meng, Y.. OPTIMIZATION OF PROCESSING TECHNOLOGY FOR PENTAERYTHRITYL
TETRABROMIDE WITH ORTHOGONAL DESIGN[J]. Fiber Reinforced Plastics/Composites, 2010, 210(1): 67-69.

[1]	黄世俊, 童跃进, 苏志忠, 陈银桂, 艾生儿, 张振伟. 木质素改性酚醛树脂的合成及其模塑料的性能[J]. 复合材料科学与工程, 2021, 0(11): 102-107.
[2]	蔡正林, 马鹏, 李进, 康少付, 张佃平. 多因素协同对GF/VE复合材料螺栓连接强度的影响研究[J]. 复合材料科学与工程, 2020, 0(12): 54-58.
[3]	王庆涛, 朱家强, 李炜. VARTM和RTM工艺模拟仿真比较[J]. 复合材料科学与工程, 2013, 0(6): 12-15.
[4]	王庆涛, 李炜. 添加ATH 的UPR 树脂粘度特性研究[J]. 复合材料科学与工程, 2013, 0(5): 25-27.