溶液中一步合成辛烯功能化的硅纳米粒子

复合材料科学与工程 ›› 2013, Vol. 0 ›› Issue (8): 51-54.

溶液中一步合成辛烯功能化的硅纳米粒子

赵庆鹏, 董旭, 杲云, 潘肇琦^*

华东理工大学材料科学与工程学院,上海 200237

收稿日期:2013-01-28 出版日期:2013-11-28 发布日期:2022-03-22
通讯作者: 潘肇琦,男,高级工程师,zhqpan@ecust.edu.cn。
作者简介:赵庆鹏(1987-),男,硕士,主要从事硅纳米粒子方面的研究。

ONE-STEP SYNTHESIS OF OCTYLENE TERMINATED SILICON NANOPARTICLES BY A SOLUTION ROUTE

ZHAO Qing-peng, DONG Xu, GAO Yun, PAN Zhao-qi^*

School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237, China

Received:2013-01-28 Online:2013-11-28 Published:2022-03-22

摘要/Abstract

摘要： 本文以氢化铝锂为还原剂在溶液中还原四氯化硅和辛烯三氯硅烷体系,一步合成出辛烯封端硅纳米粒子,采用透射电子显微镜(TEM)表征硅纳米粒子的形貌和尺寸分布,采用紫外-可见吸收光谱和荧光光谱表征硅纳米粒子的光学性能,通过傅里叶变换红外光谱(FTIR)和核磁共振氢谱(¹H NMR)表征硅纳米粒子表面基团的化学结构。TEM 表明硅纳米粒子的平均粒径为5.07 ±0.80nm,光学性能表征证明辛烯封端硅纳米粒子具有强烈的光致发光现象,¹HNM 和FTIR证明辛烯基团以Si-C键连接在硅纳米粒子表面,为进一步制备核壳型硅纳米粒子和高分子复合型荧光生物材料打下了良好基础。

关键词: 硅纳米粒子, 表面修饰, 荧光

Abstract: A one-step synthesis, octylene terminated silicon nanoparticles were prepared via co-reduction of silicon tetrachloride and octenyltrichlorosilane using LiAlH4. The particle size and distribution were investigated by transmission electron microscopy. The optical properties were analyzed with UV-visible absorption and fluorescence spectroscopy. Their surface chemistry was characterized using fourier transform infrared spectroscopy and nuclear magnetic resonance spectroscopy. TEM showed that the average diameter of silicon quantum dots was 5.07 ±0.80nm. Optical characterization proved the highly photoluminescence of octylene terminated silicon quantum dots. ¹H NMR and FTIR indicated that octylene group was connected to the surface of silicon nanoparticles with Si-C bond. These results lay the foundation for the further preparation and application of core-shell type silicon nanoparticles and polymer composite fluorescence biological materials.

Key words: silicon nanoparticles, surface modification, fluorescence

中图分类号:

TB332

赵庆鹏, 董旭, 杲云, 潘肇琦. 溶液中一步合成辛烯功能化的硅纳米粒子[J]. 复合材料科学与工程, 2013, 0(8): 51-54.

ZHAO Qing-peng, DONG Xu, GAO Yun, PAN Zhao-qi. ONE-STEP SYNTHESIS OF OCTYLENE TERMINATED SILICON NANOPARTICLES BY A SOLUTION ROUTE[J]. COMPOSITES SCIENCE AND ENGINEERING, 2013, 0(8): 51-54.

参考文献

[1] A P Alivisatos. Semiconductor clusters,nanocrystals,and quantum dots[J]. Science,1996,271: 933-937.
[2] K H Low,C H Li,V A L Roy,et al. Homoleptic copper(I)phenylselenolate polymer as a single-source precursor for Cu2Se nanocrystals. Structure,photoluminescence and application in field-effect transistor[J]. Chem Sci,2010,1: 515-518.
[3] J G C Veinot. Synthesis,surface functionalization,and properties of freestanding silicon nanocrystals[J]. Chem Commun,2006,0: 4160-4168.
[4] A M Derfus,W C W Chan,S N Bhatia. Probing the Cytotoxicity of Semiconductor Quantum Dots[J]. Nano Letters,2004,4(1): 11-18.
[5] M Kondoh,S Araragi,K Sato,et al. Cadmium induces apoptosis partly via caspase-9 activation in HL-60 cells[J]. Toxicology, 2002,170(1-2): 111-117.
[6] J L Heinrich,C L Curtis,G M Credo,et al. Luminescent colloidal silicon suspensions from porous silicon[J]. Science,1992,255(5040): 66-68.
[7] I Umezu,I Kondo,A Sugimura. Formation of surface stabilized Si nanocrystal by pulsed laser ablation in hydrogen gas[J]. Applied Physics A: Materials Science & Processing, 2008, 93(3): 717-720.
[8] A S Heintz,M J Fink,B S Mitchell. Mechanochemical Synthesis of Blue Luminescent Alkyl/Alkenyl-Passivated Silicon Nanoparticles[J]. Advanced Materials,2007,19(22): 3984-3988.
[9] X Li,Y He,S S Talukdar,et al. Process for Preparing Macroscopic Quantities of Brightly Photoluminescent Silicon Nanoparticles with Emission Spanning the Visible Spectrum[J]. Langmuir.,2003,19(20),8490-8496.
[10] L Mangolini,E Thimsen,U Kortshagen. High-Yield Plasma Synthesis of Luminescent Silicon Nanocrystals[J]. Nano Lett. 2005,5(4): 655-659.
[11] J J Watkins,T J McCarthy. Polymer/Metal Nanocomposite Synthesis in Supercritical CO₂[J]. Chem Mater,1995,7(11): 1991-1994.
[12] R K Baldwin,K A Pettigrew,E Ratai,et al. Solution reduction synthesis of surface stabilized silicon nanoparticles[J]. Chem Commun, 2002, 0: 1822-1823.
[13] D Arquier,G Calleja,G Cerveau,et al. A new solution route for the synthesis of silicon nanoparticles presenting different surface substituents[J]. C R Chimie,2007,10: 795-802.
[14] C S Yang,R A Bley,S M Kauzlarich,et al. Synthesis of Alkyl-Terminated Silicon Nanoclusters by a Solution Route[J]. J Am Chem Soc,1999,121: 5191-5195.
[15] J Choi,NS Wang,V Reipa. Electrochemical Reduction Synthesis of Photoluminescent Silicon Nanocrystals[J]. Langmuir,2009,25(12): 7097-7102.
[16] A Shiohara,S Hanada,S Prabakar,et al. Chemical Reactions on Surface Molecules Attached to Silicon Quantum Dots[J]. J Am Chem Soc,2010,132: 248-253.
[17] L Ruizendaal,S P Pujari,V Gevaerts,et al. Biofunctional Silicon Nanoparticles by Means of Thiol-Ene Click Chemistry[J]. Chemistry-An Asian Journal,2011,6: 2776-2786.