环氧树脂改性双马来酰亚胺复合材料力学性能及耐热性能研究

摘要/Abstract

摘要： 为了探究环氧树脂(EP)对双马来酰亚胺树脂(BMI)的增强增韧效果,分别采用4种EP:AFG-90、TDE-85、E-14、D-17,用以改性BMI树脂基体,并同碳纤维方格布(CF)制成了CF/BMI-EP复合材料(CM)。采用差示扫描量热分析(DSC)测试了BMI和4组EP改性BMI的固化曲线和树脂固化后的玻璃化转变温度(Tg);采用傅立叶转换红外光谱仪(FTIR)测试了树脂体系固化后的红外吸收光谱;采用万能力学试验机测试了各组CM的弯曲性能和冲击韧性,观察记录了试样破坏的断裂形貌;采用扫描电镜(SEM)对CM试样的层间断面进行了形貌分析。研究发现,EP和BMI先后进行相对独立的固化,混合树脂相容性良好。实验发现,TDE-85的增强效果最佳,D-17的增韧效果最佳,并满足增强增韧规律。AFG-90、TDE-85、D-17改性BMI的T_g都在200℃以上,表明EP在改性BMI的同时并未牺牲耐热性。

关键词: 双马来酰亚胺, 环氧树脂, 增韧, 增强, 预浸料, 复合材料

Abstract: In order to study the properties of epoxy (EP) resin modified bismaleimide (BMI) resins, four kinds of epoxy resin: AFG-90, TDE-85, E-14 and D-17 modified BMI resins were prepared. BMI and EP modified BMI resins were processed into prepregs with carbon fiber (CF) grid cloth. The prepregs were made into composites through laminated molding. The infrared absorption spectrum of cured resin system was tested. The curing curves of unmodified and four EP modified resins and the glass transition temperature (T_g) was tested by DSC. The bending strength and impact toughness of the samples were test by a universal mechanical test machine. And the damaged morphology were observed and recorded by SEM. The results indicate that the EP and BMI are cured on different temperature with good compatibility. It was found that the enhancement of TDE-85 group was best, and the D-17 has the best toughening effect which fits the strengthing and toughing rules. The T_gs of AFG-90,TDE-85,D-17 were higher than 200℃, which suggests that EP modified BMIs did not sacrifice their heat resistance.

Key words: bismaleimide, epoxy, enhancement, toughening, prepreg, composite

中图分类号:

TB332

王居临, 王钧. 环氧树脂改性双马来酰亚胺复合材料力学性能及耐热性能研究[J]. 复合材料科学与工程, 2014, 0(5): 25-31.

WANG Ju-lin, WANG Jun. STUDY OF MECHANICAL PROPERTIES AND HEAT RESISTANCE OF EPOXY RESIN MODIFIED BISMALEIMIDE COMPOSITES[J]. COMPOSITES SCIENCE AND ENGINEERING, 2014, 0(5): 25-31.

参考文献

[1] Pei Sun, Yan Zhao, Yunfeng Luo, Lili Sun. Effect of temperature and cyclic hydrothermal aging on the interlaminar shear strength of carbon fiber/bismaleimide (BMI) composite[J]. Materials and Design, 2011, 32:4341-4347.
[2] John Montesano,Marina Selezneva,et al.Elevated temperature off-axis fatigue behavior of an eight-harness satin woven carbon-fiber/bismaleimide laminate[J].Composites Part A,2012,43(9):1454-1466.
[3] Li-Rong Bao, Albert F. Yee. Effect of temperature on moisture absorption in bismaleimide resin and its carbon fiber composites[J]. Polymer, 2002, 43(14):3987-3997.
[4] S. Premkumar, C. Karikal Chozhan, M. Alagar.Studies on thermal, mechanical and morphological behaviour of caprolactam blocked methylenediphenyl diisocyanate toughened bismaleimide modified epoxy matrices[J] . European Polymer Journal, 2008, 44(8):2599-2607.
[5] 李鹏, 张衍等. 微波法合成新型双酚A 二苯醚型双马来酰亚胺研究[J]. 玻璃钢/复合材料, 2013,(4):12-15.
[6] 张承双, 王百亚等. 新型改性双马来酰亚胺树脂(J) 及PBO/JM复合材料力学性能、耐热性能研究[J]. 玻璃钢/复合材料, 2012,(6): 14-18.
[7] 周伟, 方俊等. 一种新型膨胀单体预聚物的制备及其改性BDM/DABPA共混体的研究[J]. 玻璃钢/复合材料,2013,(5): 14-18.
[8] M. Akay, G.R. Spratt.Evaluation of thermal ageing of a carbon fiber reinforced bismalemide[J].Composites Science and Technology, 2008,68(15): 3081-3086.
[9] Xiao Hua, Jing Fan, et al. Enhancement of the processibility of bismaleimide resins via copolymerization with allyl organo-boron compounds[J]. Journal of Materials Processing Technology, 1999, 89-90: 544-549.
[10] Moran Wanga, Qinjun Kang, et al.Thermal conductivity enhancement of carbon fiber composites[J]. Applied Thermal Engineering, 2009, 29(2-3): 418-421.
[11] Satoshi Kobayashia, Nobuo Takedab. Experimental characterization of microscopic damage behavior in carbon/bismaleimide composite-effects of temperature and laminate configuration[J]. Composites Part A: Applied Science and Manufacturing, 2002, 33(11): 1529-1538.
[12] Xian XJ,Choy CL. The Interlaminar Fracture-behavior And Toughening Mechanisms of New Carbon-fiber-reinforced Bismaleimide Composites[J].Composites, 1995, 26(1): 33-39.
[13] Joung-Man Park, Jin-Won Kim, et al. Interfacial evaluation and micro failure mechanisms of single carbon fiber/bismaleimide (BMI) composites by tensile and compressive fragmentation tests and acoustic emission[J]. Composites Science and Technology, 2002, 62: 743-756.
[14] Marie-Florence Grenier-Loustalot, Louis Da Cunha. Eutectic mixture of two bismaleimide monomers: Thermal and mechanistic study in thermal tenstate[J]. Polymer, 1997, 38(26): 6303-6315.
[15] Ezio Martuscelli, Pellegrino Musto,et al. A polymer network of unsaturated polyester and bismaleimide resins: Kinetics, mechanism and molecular structure[J]. Polymer, 1994, 37(18): 4025-4032.
[16] Xiaoyun Liu, Yingfeng Yu, Shanjun Li.Viscoelastic phase separation in polyethersulfone modified bismaleimide resin[J]. European Polymer Journal, 2005, 42(4):835-842.
[17] Hongfei ZHENG, Zhihong LIa. Bismaleimide Modified by Allyl Novolak for Superabrasives[J]. Chinese Journal of Chemical Engineering,2007,15(2):302-304.
[18] Yan Zhang, Junjun Lv, Yujian Liu. Preparation and characterization of a novel fluoride-containing bismaleimide with good processability[J]. Polymer Degradation and Stability, 2012, 97(4):626-631.
[19] Li Yuan, Aijuan Gu, Guozheng Liang, et al. Microcapsule-modified bismaleimide (BMI) resins[J]. Composites Science and Technology, 2008, 68(9):2107-2113.
[20] 闻荻江. 复合材料原理[M]. 武汉: 武汉理工大学出版社, 1988. 6-12.
[21] 沈观林, 胡更开.复合材料力学[M]. 北京: 清华大学出版社, 2006.9.
[22] 梁基照. 聚合物复合材料增强增韧理论[M]. 广州: 华南理工大学出版社, 2012.