内埋元件复合材料层合板分层损伤的试验及数值研究

复合材料科学与工程 ›› 2014, Vol. 0 ›› Issue (6): 4-11.

• 基础研究 • 下一篇

内埋元件复合材料层合板分层损伤的试验及数值研究

乔文静¹, 肖毅^1*, 福田博², 八田博志³, 薛元德¹

1.同济大学航空航天与力学学院,上海200092;
2.东京理科大学,野田278-8510;
3.日本宇宙航空研究开发机构 JAXA,相模原252-5210

收稿日期:2014-01-10 出版日期:2014-06-28 发布日期:2021-09-14
通讯作者: 肖毅(1960-),男,教授,博士生导师,主要从事复合材料力学、结构强度分析与设计研究,y_xiao@tongji.edu.cn。
作者简介:乔文静(1987-),女,硕士,主要从事内埋元件复合材料的损伤失效分析研究。

AN EXPERIMENTAL AND NUMERICAL INVESTIGATION ON THE DELAMINATION IN COMPOSITE LAMINATES WITH EMBEDDED DEVICES

QIAO Wen-jing¹, XIAO Yi^1*, Fukuda Hiroshi², HATTA Hiroshi³

1. School of Aerospace Engineering and Applied Mechanics, Tongji University, Shanghai 200092, China;
2. Tokyo University of Science, Noda 278-851, Japan;
3. Japan Aerospace Exploration Agency (JAXA), Sagamihara 252-5210, Japan

Received:2014-01-10 Online:2014-06-28 Published:2021-09-14

摘要/Abstract

摘要： 功能器件集成于结构材料内是实现多功能结构一体化设计的一个重要途径。然而集成后往往导致结构系统中产生几何不连续界面,成为失效的起点,是降低原有结构性能和破坏结构完整性的主要原因。本文通过试验观察及数值分析探讨了内埋元件对其复合材料结构完整性影响的一些关键因素。拉伸试验中采用声发射技术并结合不同载荷阶段下的内部损伤观察,确立了损伤演化与拉伸性能退化的关系。结果表明,埋置件与复合材料间的分层损伤是导致结构拉伸性能退化的主要机制,分层扩展阻力取决于与埋置件相邻层的纤维取向角度。数值分析中利用有限元软件ABAQUS建立了二维平面应变有限元模型,分析了埋置件附近的应力分布,并基于断裂力学理论分析了分层损伤扩展行为。数值结果表明,引入不同临界能量释放率值,可以很好地模拟“裸界面”与“摩擦界面”对裂纹扩展速率的不同效应。

关键词: 多功能结构, 结构完整性, 分层损伤, 有限元分析, 断裂力学

Abstract: Functional devices integrated within the structural materials are a key way to implement and design the multifunctional materials and structures. However, the embedded device in a composite structure would generally cause a geometric discontinuity that result in a significant effect on the structural integrity. Some of the key issues in affecting the structural integrity have been explored experimentally and numerically in this paper. During static tensile testing, the damage evolution was monitored by acoustic emission measurement, and several specimens were observed through optical micrograph at different load levels to determine the progressive damage development. Testing results show that delamination at the interface between composite and integrated device is a significant damage mechanism in tensile performance degradation, and the delamination propagation depends on the ply angle of SUS/θ interface. A two-dimensional plane strain finite element model using ABAQUS code was developed to study damage initiation using stress analysis and the behavior for delamination propagation using a fracture mechanics approach. Numerical results show that the different effects of "slipping" and "frictional" on crack propagation can be modeled by introducing different critical release rate.

Key words: multifunctional structures, structural integrity, delamination, finite element analysis, fracture mechanics

中图分类号:

TB332

乔文静, 肖毅, 福田博, 八田博志, 薛元德. 内埋元件复合材料层合板分层损伤的试验及数值研究[J]. 复合材料科学与工程, 2014, 0(6): 4-11.

QIAO Wen-jing, XIAO Yi, Fukuda Hiroshi, HATTA Hiroshi. AN EXPERIMENTAL AND NUMERICAL INVESTIGATION ON THE DELAMINATION IN COMPOSITE LAMINATES WITH EMBEDDED DEVICES[J]. COMPOSITES SCIENCE AND ENGINEERING, 2014, 0(6): 4-11.

参考文献

[1] Gibson R F. A review of recent research on mechanics of multifunctional composite materials and structures[J]. Composite structures, 2010, 92(12): 2793-2810.
[2] Kim K S, Breslauer M, Springer G S. The effect of embedded sensors on the strength of composite laminates[J]. Journal of reinforced plastics and composites, 1992, 11(8): 949-958.
[3] Mall S, Coleman J M. Monotonic and fatigue loading behavior of quasi-isotropic graphite/epoxy laminate embedded with piezoelectric sensor[J]. Smart Materials and Structures, 1998, 7(6): 822-832.
[4] Eaton N C, Drew R C, Geiger H. Finite element stress and strain analysis in composites with embedded optical fiber sensors[J]. Smart Materials and Structures, 1995, 4(2): 113-117.
[5] Shivakumar K, Bhargava A. Failure mechanics of a composite laminate embedded with a fiber optic sensor[J]. Journal of composite materials, 2005, 39(9): 777-798.
[6] Ghezzo F, Huang Y, Nemat-Nasser S. Onset of resin micro-cracks in unidirectional glass fiber laminates with integrated SHM sensors: experimental results[J]. Structural Health Monitoring, 2009, 8(6): 477-491.
[7] Huang Y, Ghezzo F, Nemat-Nasser S. Onset of resin micro-cracks in unidirectional glass fiber laminates with integrated SHM sensors: numerical analysis[J]. Structural Health Monitoring, 2009, 8(6): 493-507.
[8] Wang M, Laird C. Characterization of microstructure and tensile behavior of a cross-woven C-SiC composite[J]. Acta materialia, 1996, 44(4): 1371-1387.
[9] Surgeon M, Vanswijgenhoven E, Wevers M, et al. Acoustic emission during tensile testing of SiC-fibre-reinforced BMAS glass-ceramic composites[J]. Composites Part A: Applied Science and Manufacturing, 1997, 28(5): 473-480.
[10] 常岩军,矫桂琼,张克实,等. 3D C/SiC 复合材料拉伸性能的声发射研究[J]. 复合材料学报, 2010, 27(6): 82-87.
[11] 周伟,马力辉,张洪波,等. 风电叶片复合材料弯曲损伤破坏声发射监测[J]. 无损检测, 2011, 33(11): 33-37.
[12] 林松, 王俊锋, 孙文文, 等. 薄壁铝内衬缠绕高压复合材料气瓶的疲劳及爆破性能研究[J]. 玻璃钢/复合材料, 2012 ,(5): 65-70.
[13] 乔文静,肖毅,闫亚萍,等. 埋植元件复合材料层合板分层损伤的数值分析[C]//第17届全国复合材料学术会议论文集. 北京: 中国航空学会编, 2012: 282-285.
[14] 乔文静,朱琳,肖毅,等. 埋植元件对复合材料结构完整性的影响[C]//中国力学大会-2013 论文摘要集. 西安: 中国力学学会办公室编, 2013: CD-ROM A31-0383.
[15] 乔文静,肖毅,朱琳,等.埋置元件复合材料层合板的分层损伤[J]. 纤维复合材料,2013, (3): 39-43.
[16] Krueger R. The Virtual Crack Closure Technique: History, Approach and Applications [R]. American Society of Mechanical Engineers, 2004, 57(2): 109-143.
[17] 陈春露, 刘文博, 张璐, 等. 复合材料层合板分层疲劳性能研究进展[J]. 玻璃钢/复合材料, 2012, (1): 83-86.
[18] 陈玉良, 程宸, 万水, 等. 基于虚拟裂纹闭合法计算组合材料的应变能释放率[J]. 玻璃钢/复合材料, 2013, (3): 8-12.
[19] Camanho P P, Davila C G, Pinho S T. Fracture analysis of composite co‐cured structural joints using decohesion elements[J]. Fatigue & fracture of engineering materials & structures, 2004, 27(9): 745-757.
[20] 朱琳. 埋植元件复合材料层合板的层间断裂韧性[D]. 上海:同济大学,2013.

内埋元件复合材料层合板分层损伤的试验及数值研究

AN EXPERIMENTAL AND NUMERICAL INVESTIGATION ON THE DELAMINATION IN COMPOSITE LAMINATES WITH EMBEDDED DEVICES

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	刘志, 张彬, 赵微微, 张勇. 聚氨酯复合材料步行板结构设计及力学性能研究[J]. 复合材料科学与工程, 2022, 0(7): 103-106.
[2]	杨智勇, 刘清念, 孙建波, 解永杰, 左小彪, 张建宝. 铺层角度偏差对曲面复合材料层合板形面轮廓的影响分析[J]. 复合材料科学与工程, 2022, 0(6): 17-26.
[3]	田会方, 任政, 吴迎峰, 张国武. 纤维缠绕罐工装杆旋拧装置设计与分析[J]. 复合材料科学与工程, 2022, 0(6): 105-110.
[4]	张若男, 陈建稳. 经编织物膜材偏轴中心撕裂行为及破坏机理[J]. 复合材料科学与工程, 2022, 0(5): 28-36.
[5]	梁旭豪, 吴鑫锐, 张砚达, 沈峰, 王晓蕾, 白瑞祥. 复合材料杆件接头的结构设计与力学研究[J]. 复合材料科学与工程, 2022, 0(5): 103-109.
[6]	彭昶玮, 黄君, 吴宇, 叶太智, 黄立新. 基于柔性结点梁单元和分层法的石墨烯/环氧树脂纳米复合材料力学性能预测[J]. 复合材料科学与工程, 2022, 0(4): 18-26.
[7]	周满清, 张智梅, 程雯. 外贴CFRP加固RC连续梁的弯矩重分布性能研究[J]. 复合材料科学与工程, 2022, 0(2): 31-37.
[8]	庄羊澎, 文子豪, 江晟达, 魏仲委, 赵西帅, 罗楚养. 耐高温复合材料舵面根部结构设计与验证[J]. 复合材料科学与工程, 2022, 0(2): 45-51.
[9]	蒋朕琦, 黄文健, 曹诗宇, 吴超群. 不同刀具对超声辅助钻削CFRP分层损伤的影响研究[J]. 复合材料科学与工程, 2022, 0(2): 56-61.
[10]	何振鹏, 邓殿凯, 刘国峰, 孙爱俊, 钱俊泽, 黎柏春, 胡艺馨, 杨帆. 基于内聚力模型的复合材料裂纹扩展研究[J]. 复合材料科学与工程, 2022, 0(1): 5-12.
[11]	滕靓媚, 黄君, 黄立新. 基于分层法石墨烯增强功能梯度梁的有限元分析[J]. 复合材料科学与工程, 2022, 0(1): 13-21.
[12]	肖剑雄, 周向, 申政. 高速永磁电机转子碳纤维护套张力缠绕仿真分析[J]. 复合材料科学与工程, 2022, 0(1): 68-72.
[13]	钱清锋, 邓安仲, 李飞, 罗盛, 高训鹏, 施霖. GFRP支撑结构扣件节点转动刚度研究[J]. 复合材料科学与工程, 2021, 0(7): 11-16.
[14]	李磊, 宋贵宾, 郑华勇, 程鹏飞, 赵剑. 基于Puck准则的复合材料层压板低速冲击数值分析与试验验证[J]. 复合材料科学与工程, 2021, 0(6): 20-25.
[15]	温宇立, 潘美萍, 夏立鹏, 郑愚. 基于CFRP的柔性装配式圬工拱桥结构承载及装配过程的有限元分析[J]. 复合材料科学与工程, 2021, 0(4): 75-82.