反应型含磷阻燃剂对不饱和树脂阻燃性能的研究

复合材料科学与工程 ›› 2015, Vol. 0 ›› Issue (3): 11-14.

反应型含磷阻燃剂对不饱和树脂阻燃性能的研究

程刘峰¹, 王钧^1*, 刘伟²

1.武汉理工大学材料科学与工程学院,湖北武汉 430070;
2.常州百思通复合材料有限公司,江苏常州 213022

收稿日期:2014-09-26 出版日期:2015-03-28 发布日期:2021-09-13
通讯作者: 王钧(1963-),男,教授,博士生导师,主要从事复合材料方面的研究,wgdfrp@whut.edu.cn。
作者简介:程刘峰(1990-),男,硕士在读,主要从事阻燃高分子材料方面的研究。

STUDY ON THE FLAME RESISTANCES OF THE REACTIVE PHOSPHORUS-CONTAININGFLAME RETARDANT TO UNSATURATED RESIN

CHENG Liu-feng¹, WANG Jun^1*, LIU Wei²

1. School of Materials Science and Engineering,Wuhan University of Technology,Wuhan 430070,China;
2. Changzhou Bamstone Composite Material Limited Company, Changzhou 213022, China

Received:2014-09-26 Online:2015-03-28 Published:2021-09-13

摘要/Abstract

摘要： 本文以羟乙基甲基丙烯酸酯磷酸酯(HEMAP)作为不饱和树脂的反应型含磷阻燃剂,研究其对不饱和树脂阻燃性能的影响。当不饱和树脂加入5份HEMAP后,固化物的极限氧指数为32.5。热重分析结果表明,当不饱和树脂加入HEMAP量从0增加到20份时,氮气下10%失重温度和最大分解温度明显降低,P-O-C键的提前分解产生磷酸类物质,有效阻止了不饱和树脂的进一步分解,800℃残炭率从3.8%提高到31.4%;空气下500℃下初级残炭率从20.6%提高到46.3%。用动态热机械分析仪测试了树脂浇铸体损耗因子,得到树脂体系的玻璃化转变温度,加入5份HEMAP后树脂体系的Tg从120.9℃提高到122℃。

关键词: 反应型, 含磷阻燃剂, 不饱和树脂, 阻燃

Abstract: A reactive phosphorus-containing fire retardant, 2-hydroxyethyl methacrylate phosphate (HEMAP), was added to the unsaturated resin to improve its flame retardant properties. The cured unsaturated resin reached limiting oxygen index of 32.5 as added 5 parts of HEMAP. Thermal properties of unsaturated resin were studied by means of TG and DTG. Decomposition temperature of 10% mass loss and maximum weight loss both dropped with the increase of HEMAP from 0 to 20 parts by weight. However, formation of phosphorus-containing acid from decomposition of P-O-C bonds inhibited effectively further decomposition of the unsaturated resin. As the HEMAP content increased, the char yield increased from 3.8% to 31.4% at 800℃ in N₂ atmospheres, and the carbonaceous char yield increased from 0 to 4 at 500℃ in air atmosphere. The glass transition temperature (Tg) was measured by dynamic mechanical thermal analysis (DMA). The Tg of different unsaturated resins increased from 120.9℃ to 122℃ after added 5 parts of HEMAP.

Key words: reactive type, phosphorus-containing flame retardant, unsaturated resin, flame retardant

中图分类号:

TB332

程刘峰, 王钧, 刘伟. 反应型含磷阻燃剂对不饱和树脂阻燃性能的研究[J]. 复合材料科学与工程, 2015, 0(3): 11-14.

CHENG Liu-feng, WANG Jun, LIU Wei. STUDY ON THE FLAME RESISTANCES OF THE REACTIVE PHOSPHORUS-CONTAININGFLAME RETARDANT TO UNSATURATED RESIN[J]. COMPOSITES SCIENCE AND ENGINEERING, 2015, 0(3): 11-14.

参考文献

[1] 齐双春. 近年来阻燃不饱和聚酯树脂的研究进展[J]. 热固性树脂,2011,26(2):55-59.
[2] 汪海波,王锦堂. 反应型阻燃剂合成及在不饱和树脂中的应用[J]. 南京化工大学学报,2000,22(5):50-52.
[3] ES Park,et al. Synthesis of Acryl Phosphate Antistatic Agent and Its Effect on the Antistatic, Thermal and Mechanical Properties of PMMA[J].Macromolecular Research,2007,15(7):617-622.
[4] Xie Shaobo, et al. Influence of Annealing Treatment on the Heat Distortion Temperature of Nylon-6/montmorillonite nanocomposites [J]Polymer Engineering and Science,2005,45(9):1247-1253.
[5] E Kandare, et al. Study of the thermal decomposition of flame-retarded unsaturated polyester resins by thermogravimetric analysis and Py-GC/MS [J].Polymer Degradation and Stability, 2008, 93: 1996-2006.
[6] YL Liu, et al. Phosphorus-containing polyaryloxydiphenylsilanes with high flame retardance arising from a phosphorus-silicon synergistic effect[J].Polymer international,2003,52(8): 1256-1261.
[7] H Chen, et al. Synthesis and characterizations of novel phosphorous-nitrogen containing poly(ether sulfone)s[J]. Polymer Degradation and Stability, 2011, 96: 197-203.
[8] Zhang, H. Q., Farris, R. J., Westmoreland, P. R.. Low flammability and thermal decomposition behavior of poly(3,3′-dihydroxybiphenylisophthalamide) and its derivatives[J]. Macromolecules, 2003, 36: 3944-3954.
[9] Kang Dai, et al. Unsaturated polyester resins modified with phosphorus-containing. groups: Effects on thermal properties and flammability[J].Polymer Degradation and Stability, 2013,98:2033-2040.
[10] L Tibiletti, et al. Thermal degradation and fire behaviour of unsaturated polyesters filled with metallic oxides[J]. Polymer Degradation and Stability, 2011, 96: 67-75.
[11] K Dai, et al. Enhanced Properties of the Incorporation of a Novel Reactive Phosphorus-and Sulfur-Containing Flame-Retardant Monomer into Unsaturated Polyester Resin[J]. Industrial and Engineering Chemistry Research, 2012, 51: 15918-15926.
[12] 欧育湘,韩廷解,赵毅. 无卤本质阻燃热塑性共聚酯[J]. 合成树脂及塑料, 2007,24(2):82-85.
[13] 金日光,华幼卿. 高分子物理(第三版)[M]. 北京: 化学工业出版社, 2006. 66-69.

[1]	刘燕峰, 刘青曼, 陈旭. 阻燃植物纤维蜂窝芯制备及性能研究[J]. 复合材料科学与工程, 2022, 0(6): 76-80.
[2]	刘吉凯, 潘利剑. 芳纶/阻燃环氧树脂复合材料的性能研究[J]. 复合材料科学与工程, 2021, 0(2): 72-76.
[3]	南巡, 蒋文革, 周宇, 尚呈元. 一种高效无卤阻燃型液体成型环氧树脂体系[J]. 复合材料科学与工程, 2020, 0(7): 93-97.
[4]	周宇, 栾贻浩, 臧千, 凌辉. 610B无卤阻燃环氧树脂及碳纤维复合材料性能[J]. 玻璃钢/复合材料, 2020, 0(1): 60-66.
[5]	谢超, 秦岩, 黄志雄, 张博文. 空心玻璃微珠对膨胀阻燃硅橡胶复合材料性能的影响[J]. 玻璃钢/复合材料, 2020, 0(1): 95-100.
[6]	冯振宇, 樊茂华, 范保鑫, 王纳斯丹. 阻燃改性玻璃纤维环氧树脂的热响应预报方法[J]. 玻璃钢/复合材料, 2019, 0(9): 32-37.
[7]	赵志颖, 梁洪涛, 彭飞, 王少敏. ZB阻燃剂对环氧树脂复合材料性能的影响[J]. 玻璃钢/复合材料, 2018, 0(8): 80-82.
[8]	李道成,王钧,霍思奇,张斌. 纳米Al₂O₃对含磷环氧树脂体系的性能影响[J]. 玻璃钢/复合材料, 2017, 0(10): 41-45.
[9]	张琪, 敬茂, 冉起超, 顾宜. 一种适用于热熔法制备预浸料的阻燃型改性苯并噁嗪树脂的研究[J]. 玻璃钢/复合材料, 2016, 0(2): 67-70.
[10]	史汉桥, 丁常方, 孙宝岗, 程雷. SW280玻璃布/苯并噁嗪热熔法预浸料的性能研究[J]. 复合材料科学与工程, 2015, 0(2): 51-55.
[11]	李亚锋, 洪旭辉. 增韧改性对玻纤织物增强酚醛复合材料性能影响研究[J]. 复合材料科学与工程, 2015, 0(11): 71-74.
[12]	高卫卫, 曹海建, 钱坤. 玻纤增强酚醛泡沫的制备及性能研究[J]. 复合材料科学与工程, 2013, 0(9): 17-20.
[13]	王庆涛, 李炜. 添加ATH 的UPR 树脂粘度特性研究[J]. 复合材料科学与工程, 2013, 0(5): 25-27.
[14]	高卫卫, 曹海建, 钱坤, 承永刚. 聚酯纤维的阻燃及力学性能研究[J]. 复合材料科学与工程, 2013, 0(2): 65-68.
[15]	彭瑛, 刘建华, 刘敏, 雷玉龙. 不饱和树脂聚合物的耐腐蚀研究[J]. 玻璃钢/复合材料, 2009, 209(4): 39-42.