界面渗透率对厚复合材料层板流动-压实过程影响的数值分析

玻璃钢/复合材料 ›› 2017, Vol. 0 ›› Issue (10): 11-16.

界面渗透率对厚复合材料层板流动-压实过程影响的数值分析

乔炎亮^1,2,张梅^1,2*,张江涛^1,2,刘立胜^1,2,翟鹏程^1,2,张清杰³

1.武汉理工大学新材料力学理论与应用湖北省重点实验室,武汉430070;
2.武汉理工大学理学院,武汉430070;
3.武汉理工大学材料复合新技术国家重点实验室,武汉430070

收稿日期:2017-03-02 出版日期:2017-10-20 发布日期:2017-10-20
通讯作者: 张梅(1978-),女,博士,副教授,主要从事复合材料工艺研究与结构设计方面的研究,zhjiangtao@whut.edu.cn。
作者简介:乔炎亮(1991-),男,硕士,主要从事碳纤维环氧树脂基复合材料成型工艺仿真方面的研究。
基金资助:
国家自然科学基金青年基金项目(11202154);中央高校基本科研业务费专项资金资助(WUT:2016IB002)

NUMERICAL SIMULATION ON THE EFFECT OF INTERFACE PERMEABILITY ONTHE FLOW AND COMPACTION OF THICK COMPOSITE LAMINATES

QIAO Yan-liang^1,2, ZHANG Mei^1,2*, ZHANG Jiang-tao^1,2, LIU Li-sheng^1,2

1.Hubei Key Laboratory of Theory and Application of Advanced Materials Mechanics,Wuhan University of Technology, Wuhan 430070, China;
2.Department of Engineering Structure and Mechanics, School of Science,Wuhan University of Technology, Wuhan 430070, China

Received:2017-03-02 Online:2017-10-20 Published:2017-10-20

摘要/Abstract

摘要： 基于有效应力原理与达西渗流定律,建立了厚复合材料层板流动-压实过程的多场耦合有限元数值模型,通过与厚单向板试验结果的对比,验证了模型的正确性。建立了含界面层的厚正交层合板流动-压实计算模型,分析了垂直于层间界面方向的界面渗透率对正交层合板流动-压实过程的影响。通过与同等厚度单向板的分析结果对比表明,当不同方向铺层层间界面渗透率高时,厚正交层合板的流动-压实过程几乎与相同厚度单向板的流动-压实过程相同。但当层间界面的渗透率低时,会阻碍内部树脂的流动,导致正交层合板内部纤维体积含量提升慢,且越靠近内部,界面渗透率的影响越明显,最终在界面处纤维含量出现明显的跳跃分布。

关键词: 厚复合材料板, 界面, 渗透率, 流动-压实过程, 纤维含量

Abstract: Based on the effective stress theory and Darcy′s flow theory, a multi-field coupled numerical model is developed to simulate the flow and compaction of thick composite laminates. The model is verified by comparing the prediction with the experiment result of a thick unidirectional laminate. A thick cross ply composite laminate model with an interface layer is built, and is used to analyze the effect of the interface permeability on the flow and compaction process of the thick cross ply composite laminate. The calculating results of the thick cross ply composite laminate model are compared with those of the unidirectional laminate model with the same thickness. The results show that, the thick cross ply composite laminate with high interface permeability has the similar flow and compaction process with that of the thick unidirectional laminate. An interface layer with low permeability impedes the flow of the resin in the interior of the thick cross ply composite laminate, and causes a slow increase of fiber content with curing time as compared with that in a unidirectional laminate. The effect of interface layer with low permeability is more obvious in the interior of the thick cross ply composite laminate, and causes a jump in the distribution of fiber content across the interface layer at the end of the flow and compaction process.

Key words: thick composite laminates, interface, permeability, flow and compaction process, fiber content

中图分类号:

TB332

乔炎亮,张梅,张江涛,刘立胜,翟鹏程,张清杰. 界面渗透率对厚复合材料层板流动-压实过程影响的数值分析[J]. 玻璃钢/复合材料, 2017, 0(10): 11-16.

QIAO Yan-liang, ZHANG Mei, ZHANG Jiang-tao, LIU Li-sheng. NUMERICAL SIMULATION ON THE EFFECT OF INTERFACE PERMEABILITY ONTHE FLOW AND COMPACTION OF THICK COMPOSITE LAMINATES[J]. Fiber Reinforced Plastics/Composites, 2017, 0(10): 11-16.

参考文献

[1] Bogetti T A, Gillespie J J W. Process-Induced Stress and Deformation in Thick-Section Thermoset Composite Laminates[J]. Journal of Composite Materials, 1992, 26(5): 225-229.
[2] Loos A C, Springer G S. Curing of Epoxy Matrix Composites[J]. Journal of Composite Materials, 1983, 17(2): 135-169.
[3] Gutowski T G, Morigaki T, Zhong C. The Consolidation of Laminate Composites[J]. Journal of Composite Materials, 1987, 21(2): 172-188.
[4] Gutowski T G, Cai Z, Bauer S, et al. Consolidation Experiments for Laminate Composites[J]. Journal of Composite Materials, 1987, 21(7): 650-669.
[5] Dave R, Kardos J L, Dudukovic′ M P. A model for resin flow during composite processing: Part 1-general mathematical development[J]. Polymer Composites, 1987, 8(8): 29-38.
[6] Dave R. A Unified Approach to Modeling Resin Flow During Composite Processing[J]. Journal of Composite Materials, 1990, 24(1): 22-41.
[7] Smith G D, Poursartip A. A Comparison of Two Resin Flow Models for Laminate Processing[J]. Journal of Composite Materials, 1993, 27(17):1695-1711.
[8] Young W B. Consolidation and cure simulations for laminated composites[J]. Polymer Composites, 1996, 40(1): 1853-1869.
[9] Hubert P, Vaziri R, Poursartip A. A two-dimensional flow model for the process simulation of complex shape composite laminates[J]. International Journal for Numerical Methods in Engineering, 1999, 44(1): 1-26.
[10] Ganapathi A S, Joshi S C, Chen Z. Bleeder Thickness Optimization for Controlling Resin Content in Thick Laminated Composites[J]. Journal of Heat Transfer, 2013, 740(12):124504-1.
[11] 张纪奎, 张江, 马志阳,等. 厚截面层合板非同步固化的三维有限元分析[J]. 北京航空航天大学学报, 2013, 39(11): 1464-1469.
[12] 元振毅, 王永军, 张跃,等. 基于材料性能时变特性的复合材料固化过程多场耦合数值模拟[J]. 复合材料学报, 2015, 32(1): 167-175.
[13] Lam R C, Kardos J L. The permeability and compressibility of aligned and cross-plied carbon fiber beds during processing of composites[J]. Polymer Engineering & Science, 1991, 31(14): 1064-1070.
[14] 高娟娟, 张佐光, 梁子青,等. 织物预成型体厚度方向渗透特性研究[J]. 材料工程, 2006(9): 20-22.
[15] Shin D D, Hahn H T. Compaction of thick composites: Simulation and experiment[J]. Polymer Composites, 2004, 25(1):49-59.
[16] Lee W I, Loos A C, Springer G S. Heat of Reaction, Degree of Cure, and Viscosity of Hercules 3501-6 Resin[J]. Journal of Composite Materials, 1982, 16(6): 510-520.
[17] Li M, Gu Y, Zhang Z, et al. A simple method for the measurement of compaction and corresponding transverse permeability of composite prepregs[J]. Polymer Composites, 2010, 28(28): 61-70.
[18] Springer G S, Tsai S W. Thermal Conductivities of Unidirectional Materials[J]. Journal of Composite Materials, 1967, 1(2): 166-173.
[19] Bogetti T A, Gillespie J W. Two-Dimensional Cure Simulation of Thick Thermosetting Composites[J]. Journal of Composite Materials, 1991, 25(3): 239-273.
[20] Shinji Ogihara, Nobuo Takeda, Akira Kobayashi. Transverse cracking in CFRP cross-ply laminates with interlaminar resin layers[J]. Advanced Composite Materials, 1998, 7(4): 347-363.