复合材料单钉搭接单剪与双剪的挤压破坏试验研究

玻璃钢/复合材料 ›› 2017, Vol. 0 ›› Issue (4): 85-89.

复合材料单钉搭接单剪与双剪的挤压破坏试验研究

卢智先, 拓宏亮, 刘斌^*

西北工业大学航空学院,西安710072

收稿日期:2016-11-22 出版日期:2017-04-28 发布日期:2017-04-28
通讯作者: 刘斌(1986-),男,博士,主要从事复合材料胶接及胶接修理方面的研究,binbinmoon@sina.com。
作者简介:卢智先(1959-),男,高级工程师,主要从事材料和结构的力学性能测试技术方面的研究。

THE EXPERIMENTAL RESEARCH OF COMPRESSIONAL DAMAGE FOR SINGLE BOLTED JOINTS OF COMPOSITES UNDER SINGLE SHEARING AND DOUBLE SHEARING

LU Zhi-xian, TUO Hong-liang, LIU Bin^*

School of Aeronautics, Northwestern Polytechnical University, Xi′an 710072,China

Received:2016-11-22 Online:2017-04-28 Published:2017-04-28

摘要/Abstract

摘要： 复合材料机械连接在航空结构中应用广泛,在受力过程中,挤压破坏为主要关注的破坏模式。对于复合材料单钉连接结构,单剪有面外弯曲存在,双剪可视为孔边纯挤压受力模式。采用试验的方法,研究了相同孔径、厚度及铺层的单钉单剪与单钉双剪的破坏模式、挤压变形及屈服和挤压强度,发现单剪形式的二次面外弯曲对强度及变形影响大,双剪结构大幅提高了复合材料机械连接结构的屈服强度和挤压强度。在不改变铺层比例的前提下,通过改变铺层数量,探讨了层合板厚度对单钉单剪受力及破坏的影响,发现层合板的厚度增厚对单钉单剪的屈服及挤压强度提高不显著。

关键词: 复合材料, 单钉, 单剪, 双剪, 挤压

Abstract: The mechanical bolted structures of composites are widely applied in aeronautical structures. In the proceeding of loading, compressional damage dominating the damage mode needs to be concerned. For single bolted joints of composites, single shearing case exists secondary bending, but double shearing only exists pure compressional loading mode. This paper adopted experimental methodology to study damage modes, compressional deformation, yield strength and compressional strength for single shear load and double shear load of single bolted joints of different thickness. It was found that the single bolted plates of composite under single shear load of secondary bending has strong effects on strength and deformation, and the single bolted plates under double shear load enhance yield strength and compressional strength substantially. In the condition of keeping plies percentage constant, by changing plies number,force analysis and damage of single bolted joints of single shearing were investigated. The results show that making composite plates thicker cannot improve yield and compressional strength obviously.

Key words: composites, single bolt, single shearing, double shearing, compressional

中图分类号:

TB332

卢智先, 拓宏亮, 刘斌. 复合材料单钉搭接单剪与双剪的挤压破坏试验研究[J]. 玻璃钢/复合材料, 2017, 0(4): 85-89.

LU Zhi-xian, TUO Hong-liang, LIU Bin. THE EXPERIMENTAL RESEARCH OF COMPRESSIONAL DAMAGE FOR SINGLE BOLTED JOINTS OF COMPOSITES UNDER SINGLE SHEARING AND DOUBLE SHEARING[J]. Fiber Reinforced Plastics/Composites, 2017, 0(4): 85-89.

参考文献

[1] Yun J, Choi J, Kweon J. A study on the strength improvement of the multi-bolted joint[J]. Composite Structures, 2014, 108: 409-416.
[2] Camanho P P, Matthews F L. A progressive damage model for mechanically fastened joints in composite laminates[J]. Journal of Composite Materials, 1999, 33(24): 2248-2280.
[3] Tan K T, Watanabeb N, Iwahori Y, et al. Effect of stitch density and stitch thread thickness on compression after impact strength and response of stitched composites[J]. Composites Science and Technology, 2012, 72(5): 587-598.
[4] Khashaba U A, Sebaey T A, Mahmoud F F, et al. Experimental and Numerical Analysis of pinned-joints composite laminates: effects of stacking sequences[J]. Journal of Composite Materials, 2012, 47(27): 3353-3366.
[5] Hatta H, Taniguchi K, Kogo Y. Compressive strength of three-dimensionally reinforced carbon/carbon composite[J]. Carbon, 2005, 43: 351-358.
[6] Hatta H, Suzuki K, Shigei T, et al. Strength improvement by densification of C/C Composites[J]. Carbon, 2001, 39: 83-90.
[7] Li C, Crosky A. The effect of carbon fabric treatment on delamination of 2D-C/C Composites[J]. Composites Science and Technology, 2006, 66: 2633-2638.
[8] Huang C, Lee Y. Experiments and simulation of thestatic contact crush of composite laminated plates[J]. Composite Structures, 2003, 61: 265-270.
[9] Ekh J, Schn J. Effect of secondary bending on strength prediction of composite, single shear lap joints[J]. Composites Science and Technology, 2005, 65(6): 953-965.
[10] Xiao J R, Gama B A, Gillespie J W. Progressive damage and delamination inplain weave S-2 glass/SC-15 composites under quasi-static punch-shear loading[J]. Composite Structures, 2007, 78: 182-196.
[11] Camanho P P, Davila C G. Mixed-mode decohesion finite elements for the simulation of delaminatin in composite materials[J]. NASN/TM, 2002, 211737.
[12] Stocchi C, Robinson P, Pinho S T. A detailed finite element investigation of composite bolted joints with countersunk fasteners[J]. Composites: Part A, 2013, 52: 143-150.
[13] Egan B, McCarthy M A, Frizzell R M, et al. Modelling bearing failure in countersunk composite joints under quasi-static loading using 3D explicit finite element analysis[J]. Composite Structures, 2014, 108: 963-977.
[14] 韩红梅.碳/碳复合材料的力学性能及损伤演变研究[D]. 西安: 西北工业大学博士学位论文, 2002: 5-14.
[15] 廖晓玲. 三维编织碳/碳复合材料的疲劳行为以及损伤演变研究[D]. 西安: 西北工业大学博士学位论文, 2006.
[16] Adam L, Bouvet C, Castanié B, et al. Discrete ply model of circular pull-through test of fasteners in laminates[J]. Composite Structures, 2012, 94: 3082-3091.
[17] Camanho P P, Lambert M. A design methodology for mechanically fastened joints in laminated composite materials[J]. Composites Science and Technology, 2006, 66(15): 3004-3020.
[18] Standard test method for measuring the fastener pull-through resistance of a fiber-reinforced polymer matrix composite: ASTMD 733210 7332M-07[S]. 2007.
[19] 唐玉玲. 碳纤维复合材料连接结构的失效强度及主要因素分析[D]. 哈尔滨: 哈尔滨工业大学博士论文,2015.
[20] Gray P J, O′Higgins R M, McCarthy C T. Effect of thickness and laminate taper on the stiffness, strength and secondary bending of single-lap, single-bolt countersunk composite joints[J]. Composite Structures, 2014, 107: 315-324.
[21] Ekh J, Schn J, Melin G L. Secondary bending in multi fastener, composite-to- aluminium single shear lap joints[J]. Composites Part B: Engineering, 2005, 36(3): 195-208.