高应力水平下T700/MTM46复合材料层合板拉-拉疲劳性能研究

摘要/Abstract

摘要： 本文研究了T700/MTM46复合材料层合板在高应力水平下的拉-拉疲劳性能。首先开展了层合板静拉伸试验研究,得到了静拉伸强度、模量和破坏应变,各项静力性能指标分散性小,静力破坏模式以小范围内的脆性断裂为主。然后根据得到的静强度确定疲劳应力水平,开展层合板拉-拉疲劳性能试验研究,各应力水平下疲劳寿命分散性大,且并没有随应力水平高低表现出规律性;疲劳破坏模式以分层失效为主,几乎整个工作段长度内都出现了严重的分层现象;疲劳应力水平越高,破坏时刚度下降程度越小,且归一化刚度退化曲线表现出“快-慢-快”三阶段性;疲劳过程中损伤起源于90°层,且在疲劳过程中该层内的损伤扩展最为严重,0°层的损伤出现最晚,但是0°层纤维断裂预示着即将发生灾难性的疲劳破坏。

关键词: 复合材料, 疲劳, 破坏模式, 刚度退化, 损伤演化

Abstract: Tension-tension fatigue properties of T700/MTM46 composite laminates under high stress level were studied in this paper. Static tensile properties were investigated to obtain the ultimate tensile strength, modulus and failure strains. The static index has small scatter and the static failure modes are mainly characterized by the brittle fracture in a small region. Fatigue stress levels were determined by the ultimate tensile strength. Then the tension-tension fatigue tests were conducted. The scatter of fatigue life in each stress level is relatively large, which do not show clear trend with the change of the stress level. Fatigue failure modes of composite laminates are mainly serious delamination through the whole gauge length. The higher the stress level is, the more serious the stiffness decreases. Moreover, the normalized stiffness degradation curves exhibit three obvious stages characterized by "Quick-Slow-Quick" trend. The damages in fatigue loading initiate from 90° plies and show the most serious damage. Damages in 0° plies during fatigue loading appear latest. However, the fiber breakage in 0° plies indicates the coming catastrophic fatigue failure.

Key words: composite materials, fatigue, failure modes, stiffness degradation, damage evolution

中图分类号:

TB332

王育虔, 刘展, 杜金强. 高应力水平下T700/MTM46复合材料层合板拉-拉疲劳性能研究[J]. 玻璃钢/复合材料, 2019, 0(4): 31-36.

WANG Yu-qian, LIU Zhan, DU Jin-qiang. STUDY ON THE TENSION-TENSION FATIGUE PROPERTIES OF T700/MTM46 COMPOSITE LAMINATES UNDER HIGH STRESS LEVEL[J]. Fiber Reinforced Plastics/Composites, 2019, 0(4): 31-36.

参考文献

[1] Liu X Y, Han K, Bai R X, et al. Buckling measurement and numerical analysis of M-type ribs stiffened composite panel. Thin-Walled Structures, 2014, 85: 117-124.
[2] Benoit L, Gabriel L, Luc R L, et al. Environmental effects on mode II fatigue delamination growth in an aerospace grade carbon/epoxy composite. Composites: Part A, 2012, 43: 475-485.
[3] 熊华峰. 复合材料疲劳分散性与强度分散性的关系. 南京: 南京航空航天大学, 2009.
[4] Jitendra S T, Ajit D K. Stiffness degradation model for biaxial braided composites under fatigue loading. Composites: Part B, 2008, 39: 548-55.
[5] Giancane S, Panella F W, Dattoma V. Characterization of fatigue damage in long fiber epoxy composite laminates. International Journal of Fatigue, 2010, 32: 46-53.
[6] Rosa G L, Risitano A. Thermographic methodology for rapid determination of the fatigue limit of materials and mechanical components. International Journal of Fatigue, 2000, 22: 65-73.
[7] Arief Yudhanto, Naoyuki Watanbe,Yutaka Iwahori, et al. Effect of stitch density on fatigue characteristics and damage mechanisms of stitched carbon/epoxy composites. Composites: Part A, 2014, 60: 52-65.
[8] 冯培峰, 王殿富, 杜善义, 等. 层合复合材料的疲劳剩余刚度统计分布模型. 应用力学学报, 2003, 20(3): 52-55.
[9] 冯培峰, 杜善义, 王殿富, 等. 层板复合材料的疲劳剩余刚度衰退模型. 固体力学学报, 2003, 24(1): 46-52.
[10] 张应福, 傅惠民, 黎观生. 评估复合材料安全寿命的低成本方法. 复合材料学报, 1999, 16(4):142-146.
[11] 姚卫星, 宗俊达, 廉伟. 监测复合材料结构剩余疲劳寿命的剩余刚度方法. 南京航空航天大学学报, 2012, 44(5): 678-673.
[12] 廉伟, 姚卫星. 复合材料层压板剩余刚度-剩余强度关联模型. 复合材料学报, 2008, 25(5): 151-156.
[13] Standard test method for tensile properties of polymer matrix composite materials: ASTM D3039/D3039M. 2012.
[14] Standard test method for tension-tension fatigue of polymer matrix composite materials: ASTM D3479/D3479M. 2012.
[15] Hodgkinson J M. Mechanical testing of advanced fibrecomposite. New York: Woodhead publishing, 2003.
[16] Haeberle J. Strength and failure mechanisms of carbon fibre-reinforced plastics under axial compression. London: London University, 1992.
[17] 陈传尧. 疲劳与断裂. 武汉: 华中科技大学出版社, 2002.
[18] Klesnil M. Fatigue of metallic materials. Elservier Scientific Pub, 1980.
[19] Fuchs H O, Stephens R I. Metal fatigue in engineering. New York: Wiley,1980.
[20] Harris B. Fatigue in composites. Cambridge: Woodhead Publishing Ltd., 2003.