玻璃钢/复合材料 ›› 2019, Vol. 0 ›› Issue (7): 55-59.

RTM成型用水溶性芯模研制

李熠杰¹, 陈利^2*

1.天津工业大学纺织学院,天津300387;
2.天津工业大学复合材料研究所,天津300387

收稿日期:2018-10-31 出版日期:2019-07-28 发布日期:2019-07-28
通讯作者: 陈利(1971-),男,教授,博士生导师,主要研究方向为先进纺织复合材料,chenli@tjpu.edu.cn。
作者简介:李熠杰(1968-),男,硕士研究生,主要从事中空复合材料成型工艺及力学性能方面的研究。
基金资助:
天津市高等学校创新团队项目(TD13-5043)

DEVELOPMENT OF WATER-SOLUBLE CORE MOLD FOR RTM MOLDING

LI Yi-jie, CHEN Li^*

1.School of Textile Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China;
2.Tianjin Polytechnic University Institute of Composite Meterials, Tianjin 300387, China

Received:2018-10-31 Online:2019-07-28 Published:2019-07-28

摘要/Abstract

摘要： 采用两种大小不同的粒径制备了一种新型水溶性皮芯结构芯模,并对其成型性、力学性能、水溶溃散性及不同粒径制得芯模表面的粗糙度进行研究,结果表明水溶性皮芯结构芯模具有良好的成型性,强度高,并且在保证表面精度的同时有较好的水溶溃散性,综合了小粒径强度、表面精度高和大粒径水溶性好的优势,表面包覆铁氟龙耐高温胶带成功阻止树脂在复合中浸入芯模,且脱模简单。水溶性皮芯式水溶性芯模工艺可以很好地满足长径比大的芯模的要求,给开口小、长径比大的异形件制备提供了新思路。

关键词: 水溶性, 皮芯式结构芯模, 中空复合材料

Abstract: In order to develop novel hollow composite materials, a new type of skin-core structure of water-soluble core mold was prepared by using sand with different particle size, and the surface roughness of the core mold was studied by its formability, mechanical properties, water-soluble collapsibility and particle size. The results show that the skin-core structure of water-soluble core mold has good formability, high strength, and good water-soluble collapsibility while ensuring surface precision. It combines the advantages of small particle size, light weight and large particle size, and high temperature resistance. The Teflon film successfully prevented the resin from immersing in the core mold in the composite. The gradient particle size water-soluble core mold process can well meet the requirements of the core mold with large aspect ratio, and provides a new idea for the preparation of shaped parts with small opening and large aspect ratio.

Key words: water-solubles, kin-core structure, hollow-composite

中图分类号:

TB332

李熠杰, 陈利. RTM成型用水溶性芯模研制[J]. 玻璃钢/复合材料, 2019, 0(7): 55-59.

LI Yi-jie, CHEN Li. DEVELOPMENT OF WATER-SOLUBLE CORE MOLD FOR RTM MOLDING[J]. Fiber Reinforced Plastics/Composites, 2019, 0(7): 55-59.

[1]	袁铁军, 周来水, 郑伟峰, 安鲁陵. 微波固化成型三维中空复合材料结构的力学性能[J]. 玻璃钢/复合材料, 2017, 0(3): 53-59.
[2]	罗浩,陶红波,鲁先孝,郭万涛. 水溶性芯模在VARI成型工艺中的应用研究[J]. 玻璃钢/复合材料, 2017, 0(11): 77-79.
[3]	戚洪强,周正亮,张守玉,赵大娟，陈同海. 三维中空复合材料的电性能研究[J]. 玻璃钢/复合材料, 2017, 0(10): 68-71.
[4]	马立. 新型水溶性模具材料的性能及其应用研究[J]. 复合材料科学与工程, 2013, 0(3): 72-75.