固化压力对厚L形CFRP单向板纤维分布影响的实验研究

复合材料科学与工程 ›› 2020, Vol. 0 ›› Issue (2): 85-90.

固化压力对厚L形CFRP单向板纤维分布影响的实验研究

张昆桥¹, 张江涛^1*, 张梅², 翟鹏程²

1.武汉理工大学理学院新材料力学理论与应用湖北省重点实验室,武汉430070;
2.武汉理工大学工程结构与力学系,武汉430070

收稿日期:2019-04-18 出版日期:2020-02-28 发布日期:2020-02-28
通讯作者: 张江涛(1978-),男,博士,副教授,主要从事复合材料工艺仿真与损伤力学方面的研究,zhjiangtao@whut.edu.cn。
作者简介:张昆桥(1992-),男,硕士研究生,主要从事碳纤维环氧树脂基复合材料工艺与结构性能分析方面的研究。
基金资助:
武汉理工大学自主创新基金基础学科重点项目(2018IB004)

EXPERIMENTAL STUDY ON EFFECT OF CURING PRESSURE ON FIBER DISTRIBUTIONOF THICK L-SHAPED CFRP UNIDIRECTIONAL LAMINATES

ZHANG Kun-qiao¹, ZHANG Jiang-tao^1*, ZHANG Mei², ZHAI Peng-cheng²

1.Hubei Key Laboratory of Theory and Application of Advanced Materials Mechanics, School of Science,Wuhan University of Technology, Wuhan 430070, China;
2.Department of Engineering Structure and Mechanics, Wuhan University of Technology,Wuhan 430070, China

Received:2019-04-18 Online:2020-02-28 Published:2020-02-28

摘要/Abstract

摘要： 采用热压罐工艺制备了厚L形CFRP单向板,通过对其宏细观结构形貌的分析,研究压力对厚L形CFRP单向板厚度和纤维分布的影响。结果表明:采用热压罐工艺制备厚L形CFRP单向板时会出现褶皱和厚度不均匀等缺陷,预浸料层间有明显的树脂富集带。通过增加固化压力,可以降低树脂富集带的宽度,抑制厚L形CFRP单向板表面褶皱的产生,增加压实量,但会导致不同截面间纤维体积分数差异变大,外侧纤维梯度分布区变大;增加压力还会导致曲面段变薄且靠近底部纤维含量变高,靠近模具侧树脂有向平板/曲面段过渡区流动聚集的趋势。

关键词: 厚L形单向板, 热压罐工艺, 固化压力, 纤维分布

Abstract: The thick L-shaped unidirectional carbon fibre reinforced polymer composite laminates (CFRP) were manufactured by the autoclave process. Based on the analysis of macroscopic and microscopic structure morphology, the effects of autoclave pressure on the laminate thickness and fiber distribution were estimated. The results show that the out-of-plane wrinkling and nonuniform thickness distribution arise in the thick L-shaped CFRP unidirectional laminates manufactured by the autoclave process. The resin-rich regions are present between the prepregs. By increasing the autoclave pressure, the thickness of resin-rich regions between prepregs and the wrinkles in the thick L-shaped CFRP unidirectional laminates can be reduced. The thickness compaction, the fiber content difference between different sections and fiber content gradient in the region closing to the bleeder increase with the increasing the autoclave pressure, the thickness of corner section becomes smaller than that of the flat section, and fiber content near mold surface becomes higher if a high autoclave pressure is applied. Close to the mold side, the resin tends to aggregate into the flat/corner transition region.

Key words: thick L-shaped unidirectional laminate, autoclave process, curing pressure, fibre distribution

中图分类号:

TB332

张昆桥, 张江涛, 张梅, 翟鹏程. 固化压力对厚L形CFRP单向板纤维分布影响的实验研究[J]. 复合材料科学与工程, 2020, 0(2): 85-90.

ZHANG Kun-qiao, ZHANG Jiang-tao, ZHANG Mei, ZHAI Peng-cheng. EXPERIMENTAL STUDY ON EFFECT OF CURING PRESSURE ON FIBER DISTRIBUTIONOF THICK L-SHAPED CFRP UNIDIRECTIONAL LAMINATES[J]. Composites Science and Engineering, 2020, 0(2): 85-90.

参考文献

[1] Mrazova M. Advanced composite materials of the future in aerospace industry. Incas Bulletin, 2013, 5(3): 139-150.
[2] 杜善义. 先进复合材料与航空航天. 复合材料学报, 2007, 24(1): 1-12.
[3] 谢富原, 王雪明, 李敏, 等. 复合材料结构几何要素与制造缺陷的关联分析. 材料工程, 2009(S1): 84-88.
[4] Hassan M H, Othman A R, Kamaruddin S. A review on the manufacturing defects of complex-shaped laminate in aircraft composite structures. International Journal of Advanced Manufacturing Technology, 2017, 91: 4081-4094.
[5] Bloom L D, Wang J, Potter K D, et al. Damage progression and defect sensitivity: An experimental study of representative wrinkles in tension. Composites Part B-Engineering, 2013, 45(1): 449-458.
[6] Sjölander J, Hallander P,Åkermo M. Forming induced wrinkling of composite laminates: A numerical study on wrinkling mechanisms. Composites Part A: Applied Science and Manufacturing, 2016, 81: 41-51.
[7] Lightfoot J S, Wisnom M R, Potter K. A new mechanism for the formation of ply wrinkles due to shear between plies. Composites Part A: Applied Science and Manufacturing, 2013, 49: 139-147.
[8] Hallander P, Sjölander J,Åkermo M. Forming induced wrinkling of composite laminates with mixed ply material properties;an experimental study. Composites Part A: Applied Science and Manufacturing, 2015, 78: 234-245.
[9]Åkermo M, Larberg Y, Sjölander J, et al. Influence of interply friction on the forming of stacked prepreg//The 19th International Conference on Composite Materials (ICCM19). Montreal, Canada: Curran Associates, Inc., c2013: 919-928.
[10] Hubert P, Poursartip A. Aspects of the compaction of composite angle laminates: An experimental investigation. Journal of Composite Materials, 2001, 35(1): 2-26.
[11] Li Y X, Li M, Gu Y Z, et al. Numerical and experimental study on the effect of lay-up type and structural elements on thickness uniformity of L-shaped laminates. Applied Composite Materials, 2009, 16(2): 101-115.
[12] Brillant M. Out-of-autoclave manufacturing of complex shape composite laminates. Montreal Canada: McGill University, 2010.
[13] Xin C B, Gu Y Z, Li M, et al. Experimental and numerical study on the effect of rubber mold configuration on the compaction of composite angle laminates during autoclave processing. Composites Part A: Applied Science and Manufacturing, 2011, 42(10): 1353-
1360.
[14] 贺继林, 潘若阳, 王特, 等. 曲率参数对纤维增脂基复合材料构件固化压实的影响. 复合材料学报, 2016, 33(3): 551-557.
[15] Hubert P, Vaziri R, Poursartip A. A two-dimensional flow model for the process simulation of complex shape composite laminates. International Journal for Numerical Methods in Engineering, 1999, 44(1): 1-26.
[16] Shin D D, Hahn H T. Compaction of thick composites:simulation and experiment. Polymer Composites, 2004, 25(1): 49-59.
[17] Bogetti T A, Gillespie J W. Process-induced stress anddeformation in thick-section thermoset composite laminates. Journal of Composite Materials, 1992, 26(5): 626-660.
[18] Qiao Y L, Zhang J T, Zhang M, et al. Numerical analysis on the flow-compaction behaviorand the effect of interface permeability in thick composite plates during autoclave processing. Journal of Materials Science, 2018, 53: 14412-14422.
[19] Cann M T, Adams D O, Schneider C L. Characterization of fiber volume fraction gradients in composite laminates. Journal of Composite Materials, 2008, 42(5): 447-466.
[20] 邓火英, 张佐光, 顾轶卓, 等. L形层板真空袋成型缺陷的实验研究. 复合材料学报, 2007, 24(4): 34-39.