PMI泡沫夹芯复合材料湿热老化性能研究

摘要/Abstract

摘要： 通过对夹芯结构复合材料湿热老化性能的研究,探究环境对夹芯结构复合材料性能的影响。实验中采用了聚甲基丙烯酰亚胺(PMI)、玻璃纤维增强环氧树脂(SW110C/608)复合材料面板制备了PMI泡沫夹芯结构复合材料,研究了PMI泡沫夹芯结构复合材料的耐湿热老化特性,并讨论了湿热对PMI泡沫夹芯结构复合材料的压缩性能以及弯曲性能的影响。结果发现,PMI泡沫夹芯结构复合材料浸泡在水中时的饱和吸湿时间为30d,饱和吸水率为4.08%,通过Fick第二扩散定律发现水分子在PMI泡沫中的扩散系数为水分子在面板扩散系数的29.29倍,由于水分子的增塑作用以及浓度梯度扩散的影响,湿热处理后的PMI泡沫夹芯复合材料的平压强度下降了32.86%,侧压强度下降了16.73%,弯曲强度下降了23.94%。

关键词: PMI泡沫, 夹层复合材料, 湿热老化, 压缩性能, 弯曲性能

Abstract: An experimental study was performed to investigate the hygrothermal ageing mechanisms of PMI foam cored sandwich composite. To determine the effects of marine environment on the properties of sandwich composites. The polymethacrylimide (PMI) foam cored sandwich structure was prepared by using PMI foam, E-glass/epoxy resin (SW110C/608) composite panel. The moisture absorption of PMI foam cored sandwich structure, composite panel and PMI foam were investigated, and the effect of the hydrothermal condition on the compressive and flexural properties of the PMI foam cored sandwich structure was also determined. The results indicate that the saturated hygroscopic time of PMI foam cored sandwich structure is 30 days and its absorption ratio is 4.08%. The absorption behavior follows Fickian diffusion behavior and the diffusion constant for foam is about 30 times greater than those for the composite panel. Due to concentration gradient and the plasticization of water, the decrease of flatwise compression strength, edgewise compression strength and flexural strength is 32.86%, 16.73% and 23.94%, respectively.

Key words: PMI foam, sandwich structure, hydrothermal condition, compressive property, flexural property

中图分类号:

TB332

尹亮, 郑国栋, 丁常方, 朱元喆. PMI泡沫夹芯复合材料湿热老化性能研究[J]. 复合材料科学与工程, 2015, 0(8): 5-9.

YIN Liang, ZHENG Guo-dong, DING Chang-fang, ZHU Yuan-zhe. STUDY ON HYGROTHERMAL AGEING OF PMI FOAM CORED SANDWICH COMPOSITE[J]. COMPOSITES SCIENCE AND ENGINEERING, 2015, 0(8): 5-9.

参考文献

[1] Choi. L, Kim. J G, Seo I S, et al. Radar absorbing sandwich construction composed of CNT, PMI foam and carbon/epoxy composite. Composite Structures, 2012, 94: 3002-3008.
[2] Kim P C, Chin W S, Lee D G, et al. EM characteristics of the RAS composed of E-glass/epoxy composite and single dipole FSS element. Composite Structure, 2006, 75: 601-609.
[3] Rinker M, John M, Zahlen P C, et al. Face sheet debonding in CFRP/PMI sandwich structures under quasi-static and fatigue loading considering residual thermal stress. Engineering Fracture Mechanics, 2011, 78: 2835-2847.
[4] Wu J, Wang P, Huang C, et al. Hydrothermal synthesis, structure characterization and luminescence property of three porous coordination polymers using aexible tripodal amide containing linker. Inorganic Chemistry Communications, 2012, 15: 301-304.
[5] Granville D M. Moisture effects of polymethacrylimide foam and honeycomb core in sandwich/skin structures. Annu Forum Proc: Am Helicop Soc, 1987, 2: 907-914.
[6] Sharma N, Gibson R F, Ayorinde E O. Fatigue of foam and honeycomb core composite sandwich structures: a tutorial. Sandwich Struct Mater, 2006, 8: 263-319.
[7] 胡建平, 蔡吉喆, 肇研. Nomex/氰酸酯树脂夹层复合材料耐湿热性研究. 材料工程, 2010, 9: 140-146.
[8] Wang T, Vladimir S, Shankar R. Assessment of sandwich models for the prediction of sound transmission loss in unidirectional sandwich panels. Applied Acoustics, 2005, 66: 245-262.
[9] Grosveld F W, Mixon J S. Noise transmission through an acoustically treated and honeycomb-stiffened aircraft sidewall. Journal of Aircraft, 1985, 22: 434-440.
[10] Van W, Vuur A. Mechanical Properties of composite panels based on woven Sandwich-fabric preforms. Composites: partA, 2000, 31: 671-680.
[11] John B, Reghunadhan Nair C P, Mathew D, et al. Foam Sandwich Composites with Cyanate Ester Based Syntactic Foam as Core and Carbon-Cyanate Ester as Skin: Processing and Properties. Journal of Applied polymer Science, 2008, 110:1366-1374.
[12] Kishore V, Shankar R. Gradient syntactic foams: Tensile strength, modulus and fractographic features. Materials Science and Engineering A, 2005, 412: 153-158.
[13] Gupta N, Woldesenbet E. Hygrothermal studies on syntactic foams and compressive strength determination. Composite Structures, 2003, 61: 311-320.
[14] Mamalis A G, Papapostolou D P. Experimental investigation of strain rate effects on the crushing characteristics of composite sandwich panels. International Journal of Crashworthiness, 2010, 15: 581-603.
[15] McGarva L D, Astrom B T. Experimental investigation of compression moulding of glass/PA12-PMI foam core sandwich components. Composites: Part A, 1999, 30:1171-1185.
[16] Pilon, L, Fedorov, A G, Viskanta, R. Gas diffusion in closed-cell foams. Journal of Cell and Plastic, 2000, 36:451-474.
[17] David R, Veazie, Kito R. Robinson E. Effects of the marine environment on the interfacial fracture toughness of PVC core sandwich composites. Composites: Part B, 2004, 35: 461-466.
[18] Manujesh B J, Vijayalakshmi R, Sham Aan M P. Moisture absorption and mechanical degradation studies of polyurethane foam cored E-glass-reinforced vinyl-ester sandwich composites. Journal of Reinforced Plastics and Composites, 2014, 33: 479-492.
[19] Katzman H A, Castaneda R M, Lee H S. Moisture diffusion in composite sandwich structures. Composites: Part A, 2008, 39: 887-892.
[20] 董安琪, 段跃新, 肇研, 等. 湿热环境对PMI泡沫夹芯复合材料性能的影响. 复合材料学报, 2012, 29: 46-52.