含开孔与含裂缝的复合材料层压板拉伸剩余强度评估

doi:10.19936/j.cnki.2096-8000.20240228.004

摘要/Abstract

摘要： 为研究含开孔和裂缝的碳纤维增强树脂基复合材料(CFRP)层压板在拉伸载荷作用下的剩余强度,针对四种典型铺层、两类损伤形式、四种损伤尺寸的约200件试验件进行了试验研究。结果表明:对于具有相同铺层、相同宽度的复合材料层压板,开孔直径与裂缝长度相等时,两类层压板有相同的剩余强度;加载过程中,裂缝根部较早出现裂缝、分层,应力重新分配,降低了裂缝根部的应力集中。基于损伤区纤维断裂判据、经典层压板理论及复变函数理论的强度计算方法能较准确地计算出含开孔的复合材料层压板剩余强度;计算含裂缝复合材料层压板剩余强度时可将裂缝损伤等效为开孔损伤,计算结果与试验结果吻合较好。

关键词: 开孔, 裂缝, 层压板, 损伤容限, 剩余强度, 复合材料

Abstract: Experiments on about 200 composite laminates with four typical lay-ups, two kinds of damage, and four damage sizes were conducted to investigate the residual strength of composite laminates with open hole or crack. The research indicates that the residual strength of two composite laminates with open hole and crack are equal with same lay-ups and same widths of laminates when the opening diameter is equal to the crack width. Little cracks and delamination appear earlier at the root of crack during the loading process, the stress is redistributed near the root of crack, the stress concentration reduces. The method based on fiber breakage in damage zone criterion, classical laminate theory and complex variable function theory can be used to predict the residual strength of two composite laminates with open hole, the method can also be used for laminate with crack when the crack is equivalent to an open hole, the calculated results are in good agreement with the experimental results.

Key words: open hole, crack, laminate, damage tolerance, residual strength, composites

中图分类号:

TB332

汪厚冰, 邓凡臣, 魏宏艳, 李新祥, 杨胜春. 含开孔与含裂缝的复合材料层压板拉伸剩余强度评估[J]. 复合材料科学与工程, 2024, 0(2): 27-34.

WANG Houbing, DENG Fanchen, WEI Hongyan, LI Xinxiang, YANG Shengchun. Residual strength evaluation of laminates with open hole or crack under tensile load[J]. COMPOSITES SCIENCE AND ENGINEERING, 2024, 0(2): 27-34.

参考文献

[1] 中国民用航空局飞行标准司. 航空器结构持续完整性大纲: AC-121-FS-2018-65-R1[S]. 北京: 中国民用航空局飞行标准司, 2018: 1-24.
[2] 中华人民共和国国家军用标准. 军用飞机结构完整性大纲: GJB 775A-2012[S]. 北京: 总装备部军标出版发行部, 2013: 1-6.
[3] 姚武文. 带开孔与带裂纹层压板复合材料损伤容限对比研究[J]. 新技术新工艺, 2016(9): 70-71.
[4] Federal Aviation Administration, Department of Transportation. Composite aircraft structure, advisory circular: AC20-107B[S]. Washington D. C., US: Aircraft Certification Service, 2009: 12-14.
[5] ASTM. Standard test method for open-hole tensile strength of polymer matrix composite laminates: ASTM D5766[S]. West Conshohocken, PA: ASTM Internation, 2018.
[6] WALKER T H, MINGUET P J, FLYNN B W, et al. Advanced technology composite fuselage-structure performance: NASA CR-4732[R].1997.
[7] YUDHANTO A, WATANABE N, IWAHORI Y, et al. The effects of stitch orientation on the tensile and open hole tension properties of carbon/epoxy plain weave laminates[J]. Materials & Design, 2012, 35: 563-571.
[8] ARTEIRO A, CATALANOTTI G, XAVIER J, et al. Notched response of non-crimp fabric thin-ply laminates[J]. Composites Science and Technology, 2013, 79: 97-117.
[9] O'HIGGINS R M, PADHI G S, MCCARTHY M A. et al. Experimental and numerical study of the open-hole tensile strength of carbon/epoxy composites[J]. Mechanics of Composite Materials, 2004, 40(4): 269-278.
[10] FLATSCHER T, WOLFAHRT M, PINTER G, et al. Simulations and experiments of open hole tension tests-assessment of intra-ply plasticity, damage, and localization[J]. Composites Science and Technology, 2011, 72: 1090-1095.
[11] HWAN C L, TSAI K H, CHEN W L, et al. Strength prediction of braided composite plates with a center hole[J]. Journal of Composite Materials, 2011, 45(19): 1991-2002.
[12] STONE D P, SMITH L V, KOTHIDAR A. The effect of laminate fiber orientation on open-hole tension strength: AIAA 2008-2113[R].
[13] CHUAQUI T R C, NIELSEN M W D, COLTON J. et al. Effects of ply angle and blocking on open-hole tensile strength of composite laminates: A design and certification perspective[J]. Composites Part B: Engineering, 2021, 207: 108582.
[14] HALLETT S R, GREEN B G, JIANG W G, et al. An experimental and numerical investigation into the damage mechanisms in notched composites[J]. Composites Part A: Applied Science and Manufacturing, 2009, 40: 613-624.
[15] ANDREW C B, SARAH J M, LILLIAN F M. Analysis of open hole compression specimens using the CompDam continuum damage mechanics mode: NASA/TM-20205009618[R]. 2020.
[16] MOLLENHAUER D, IARVE E V, KIMB R, et al. Examination of ply cracking in composite laminates with open holes: A moire' interferometric and numerical study[J]. Composites Part A: Applied Science and Manufacturing, 2006, 37: 282-294.
[17] PANDITA S D, NISHIYABU K, VERPOEST I. Strain concentrations in woven fabric composites with holes[J]. Composite Structures, 2003, 59: 361-368.
[18] GE M M, CHENG X Q, ZHANG Q. Compressive test and numerical simulation of center-notched composite laminates with different crack configurations[J]. Polymer Composites, 2017, 10: 2631-2642.
[19] QIAO Y, SALVIATO M. Micro-computed tomography analysis of damage in notched composite laminates under multi-axial fatigue[J]. Composites Part B: Engineering, 2020, 19: 107789.
[20] WANG J, CALLUS P J, BANNISTER M K. Experimental and numerical investigation of the tension and compression strength of un-notched and notched quasiisotropic laminates[J]. Composite Structures, 2004, 64: 297-306.
[21] SONG K C, LI Y Y, ROSE C A. Continuum damage mechanics models for the analysis of progressive failure in open-hole tension laminates[Z]. AIAA, 2011-1861.
[22] DIVSE V, MARLA D, JOSHI S S. Finite element analysis of tensile notched strength of composite laminates[J]. Composite Structures, 2021, 255: 112880.
[23] RIDHA M, WANG C H, CHEN B Y, et al. Modelling complex progressive failure in notched composite laminates with varying sizes and stacking sequences[J]. Composites Part A: Applied Science and Manufacturing, 2014, 58: 16-23.
[24] SATYANARAYNA A, PRZEKOP A. Predicting failure progression and failure loads in composite open-hole tension coupons: NASA/CR-2010-216700[R].
[25] XIN L, YANG J, WU L M, et al. Mechanical simulation of open hole compressive behavior for high-modulus and high-strength composite laminates[C]//8th International Conference on Mechanical and Aerospace Engineering. 2017: 118-123.
[26] SU Z C, TAY T E , RIDHA M, et al. Progressive damage modeling of open-hole composite laminates under compression[J]. Composite Structures, 2015, 122: 507- 517.
[27] MOURE M M, OTERO F, GARCIA-CASTILLO S K, et al. Damage evolution in open-hole laminated composite plates subjected to in-planeloads[J]. Composite Structures, 2015, 133: 1048-1057.
[28] ANDREW C B. New developments in the CompDam fiber kinking model for the interaction of kinking and splitting cracks with application to open hole compression specimens[Z]. AIAA, 2021-0697.
[29] TAY T E, LIU G, TAN V B C. Damage progression in open-hole tension laminates by the SIFT-EFM approach[J]. Journal of Composite Materials, 2006, 40: 971-992.
[30] CAMANHO P P, MAIMI P, DAVILA C G. Prediction of size effects in notched laminates using continuum damage mechanics[J]. Composites Science and Technology, 2007, 67: 2715-2727.
[31] WADDOUPS M E, EISENMANN J R, KAMINSKI B E. Macroscopic fracture mechanics of advanced composite materials[J]. Journal of Composite Materials, 1971(5): 446-454.
[32] MAR L W, LIN K Y. Fracture mechanics correlation for tensile failure of filamentary composites with holes[J]. Journal of Aircraft, 1977, 7(14): 703-704.
[33] ERIKSSON I, ARONSSON C G. Strength of tensile loaded graphite/epoxy laminates containing cracks, open and filled holes[J]. Journal of Composite Materials, 1990, 24: 456-482.
[34] WHITNEYH J M, NUISMER R J. Stress fracture criteria for laminated composites containing concentrations[J]. Journal of Composite Materials, 1974(8): 253-265.
[35] NUISMER R J, WHITNEY J M. Uniaxial failure of composite laminates containing concentrations[J]. Fracture Mechanics of Composites, 1975(9): 117-142.
[36] CHEN P H, SHEN Z, WANG J Y. A new method for compression after impact strength prediction of composite laminates[J]. Journal of Composite Materials, 2001, 35(20): 589-610.
[37] CAMANHO P P, ERCIN G H, CATALANOTTI G, et al. A finite fracture mechanics model for the prediction of the open-hole strength of composite laminates[J]. Composites Part A: Applied Science and Manufacturing, 2012, 43: 1219-1225.
[38] LIU C J, NIJHOF A H J, ERNST L J, et al. A new ultimate strength model of notched composite laminates-including the effects of matrix failure[J]. Journal of Composite Materials, 2010, 44: 1335-1349.
[39] 中国航空研究院编. 复合材料结构设计手册[M]. 北京: 航空工业出版社, 2001: 370-375.
[40] KIM S Y, KOO J M, KIM D W, et al. Prediction of the static fracture strength of hole notched plain weave CFRP composites[J]. Composites Science and Technology, 2011, 71: 1671-1676.
[41] PIPES R B, GILLESPIE J W, WETHERHOLD R C. Notched strength of composite materials[J]. Journal of Composite Materials, 1979, 13: 148-160.
[42] KIM J K, KIM D S, TAKEDA N. Notched strength and fracture criterion in fabric composite plates containing a circular hole[J]. Journal of Composite Materials, 1995, 29: 982-998.
[43] MOURE M M, HERRERO-CUENCA J, GARCIA-CASTILLO S K, et al. Design tool to predict the open-hole failure strength of composite laminates subjected to in-plane loads[J]. Composite Structures, 2020, 238: 111970.