玻璃纤维/环氧树脂预浸料固化全过程的比热容和热导率研究

doi:10.19936/j.cnki.2096-8000.20240428.003

复合材料科学与工程 ›› 2024, Vol. 0 ›› Issue (4): 20-25.DOI: 10.19936/j.cnki.2096-8000.20240428.003

玻璃纤维/环氧树脂预浸料固化全过程的比热容和热导率研究

马世恒¹, 葛敬冉¹, 刘凯², 李永善¹, 梁军^1*

1.北京理工大学先进结构技术研究院,北京 100081;
2.北京理工大学宇航学院,北京 100081

收稿日期:2023-03-14 出版日期:2024-04-28 发布日期:2024-04-28
通讯作者: 梁军(1969—),博士,教授,博士生导师,研究方向为复合材料力学,liangjun@bit.edu.cn。
作者简介:马世恒(1996—),男,硕士研究生,研究方向为复合材料工艺力学。
基金资助:
国家自然科学基金(11732002,12172045)

Study on specific heat capacity and thermal conductivity of glass fiber/epoxy resin prepreg during the whole curing process

MA Shiheng¹, GE Jingran¹, LIU Kai², LI Yongshan¹, LIANG Jun^1*

1. Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing 100081, China;
2. School of Aerospace Engineering, Beijing Institute of Technology, Beijing 100081, China

Received:2023-03-14 Online:2024-04-28 Published:2024-04-28

摘要/Abstract

摘要： 通过调制温度式差示扫描量热技术(MDSC)测定了玻璃纤维/环氧树脂预浸料在固化全过程不同方向上的比热容和热导率,并建立模型来描述比热容和热导率随温度和固化度的变化。未固化和完全固化时,预浸料的比热容和热导率随着温度的增大线性增加;在固化过程中受温度和固化度的双重影响,在固化反应前期,比热容和热导率有一个突变,在温度和固化度的作用下表现出先增大后减小的趋势。此外,通过混合定律和分段线性关系来描述比热容和热导率随温度和固化度的变化关系,结果有助于提高数值模拟中参数的准确性。

关键词: 复合材料, 预浸料, 固化过程, 比热容, 热导率, 调制差示扫描量热法

Abstract: The specific heat capacity and thermal conductivity of glass fiber/epoxy resin prepreg in different directions during the curing process were measured by modulated temperature differential scanning calorimetry (MDSC), and a model was established to describe the changes of specific heat capacity and thermal conductivity with temperature and curing degree. The specific heat capacity and thermal conductivity of the prepreg increase linearly with the increase of temperature when it is not cured and fully cured. During the curing process, it is subject to the dual effects of temperature and curing degree. In the early stage of curing reaction, there is a sudden change in the specific heat capacity and thermal conductivity, which first increases and then decreases under the effect of temperature and curing degree. In addition, the relationship between specific heat capacity and thermal conductivity with temperature and curing degree is described by mixing law and piecewise linear relationship, which is helpful to improve the accuracy of parameters in numerical simulation.

Key words: composites, prepreg, curing process, specific heat capacity, thermal conductivity, MDSC

中图分类号:

TB332

马世恒, 葛敬冉, 刘凯, 李永善, 梁军. 玻璃纤维/环氧树脂预浸料固化全过程的比热容和热导率研究[J]. 复合材料科学与工程, 2024, 0(4): 20-25.

MA Shiheng, GE Jingran, LIU Kai, LI Yongshan, LIANG Jun. Study on specific heat capacity and thermal conductivity of glass fiber/epoxy resin prepreg during the whole curing process[J]. COMPOSITES SCIENCE AND ENGINEERING, 2024, 0(4): 20-25.

参考文献

[1] BOGETTI T A, GILLESPIE JR J W. Two-dimensional cure simulation of thick thermosetting composites[J]. Journal of Composite Materials, 1991, 25(3): 239-73.
[2] PARK H C, LEE S W. Cure simulation of thick composite structures using the finite element method[J]. Journal of Composite Materials, 2001, 35(3): 188-201.
[3] HOSSEINI-TOUDESHKY H, MOHAMMADI B. Thermal residual stresses effects on fatigue crack growth of repaired panels bounded with various composite materials[J]. Composite Structures, 2009, 89(2): 216-23.
[4] WANG H. Effect of spring-in deviation on fatigue life of composite elevator assembly[J]. Applied Composite Materials, 2018, 25: 1357-1367.
[5] YI S, HILTON H H. Effects of thermo-mechanical properties of composites on viscosity, temperature and degree of cure in thick thermosetting composite laminates during curing process[J]. Journal of Composite Materials, 1998, 32(7): 600-622.
[6] 阎勇, 庄茁, 周正刚, 等. 树脂比热容对复合材料固化过程数值模拟的影响[J]. 航空材料学报, 2006(2): 37-40.
[7] 杨自春. 复合材料层合结构的非线性传热分析[J]. 海军工程大学学报, 2000(5): 9-13.
[8] 陆阳, 齐俊伟, 肖军, 等. 复合材料固化工艺的直热模具温度场均匀性分析[J]. 复合材料学报, 2021, 38(9): 2946-2955.
[9] TIFKITSIS K, WINISTOERFER A, SKORDOS A. Online optimisation and active control of the cure process of thick composite laminates[J]. Journal of Manufacturing Processes, 2023, 87: 221-230.
[10] WANG Q, WANG L, ZHU W, et al. Numerical investigation of the effect of thermal gradients on curing performance of autoclaved laminates[J]. Journal of Composite Materials, 2020, 54(1): 127-138.
[11] WANG X, WANG Q, GAO L, et al. Effects of key thermophysical properties on the curing uniformity of carbon fiber reinforced resin composites[J]. e-Polymers, 2018, 18(1): 19-26.
[12] YAMASAKI H, MORITA S. Temperature dependence of isothermal curing reaction of epoxy resin studied by modulated differential scanning calorimetry and infrared spectroscopy[J]. Journal of Molecular Structure, 2016, 1124: 249-255.
[13] MORETTI L, CASTANIÉ B, BERNHART G, et al. Characterization and modelling of cure-dependent properties and strains during composites manufacturing[J]. Journal of Composite Materials, 2020, 54(22): 3109-3124.
[14] 侯进森, 叶金蕊, 王长春, 等. 碳纤维/环氧树脂预浸料固化过程中的热导率测定[J]. 复合材料学报, 2012, 29(4): 23-28.
[15] 陈咏萱, 周东山, 胡文兵. 示差扫描量热法进展及其在高分子表征中的应用[J]. 高分子学报, 2021, 52(4): 423-444.
[16] THOMAS L C. Modulated DSC^® Paper# 2 Modulated DSC^® Basics; Calculation and Calibration of MDSC^® Signals[Z]. TA Instruments Technical Papers, 2005.
[17] LEE J-Y, SHIM M-J, KIM S-W. Autocatalytic cure kinetics of natural zeolite filled epoxy composites[J]. Materials Chemistry and Physics, 1997, 48(1): 36-40.
[18] 金毅. 调制DSC技术在比热测试中的应用[J]. 炼油与化工, 2021, 32(3): 59-60.
[19] MARCUS S M, BLAINE R L. Thermal conductivity of polymers, glasses and ceramics by modulated DSC[J]. Thermochimica Acta, 1994, 243(2): 231-239.
[20] GARCÍA-MARTÍNEZ V, GUDE M, UREÑA A. Understanding the curing kinetics and rheological behaviour of a new benzoxazine resin for carbon fibre composites[J]. Reactive and Functional Polymers, 2018, 129: 103-110.
[21] SHIN D W, HWANG S S, LEE H S, et al. The change of degree of cure and specific heat capacity according to temperature of thermoset resin[J]. Composites Research, 2015, 28(3): 99-103.
[22] 杨金水. 厚截面碳纤维复合材料VIMP工艺制备与性能研究[D]. 北京: 国防科学技术大学, 2012.

玻璃纤维/环氧树脂预浸料固化全过程的比热容和热导率研究

Study on specific heat capacity and thermal conductivity of glass fiber/epoxy resin prepreg during the whole curing process

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张燚聪, 陈建稳. PVDF膜材双轴全域拉伸非线性及力学参数研究[J]. 复合材料科学与工程, 2024, 0(4): 5-13.
[2]	汪瑞, 梅启林, 丁国民, 陈述慧, 徐建蓉, 姜端洋. 褶皱石墨烯微球制备与浸润性调控及其丙酮感知研究[J]. 复合材料科学与工程, 2024, 0(4): 14-19.
[3]	曾塘玉, 马传国, 向阳, 邵士磊. BN粒子改性PVDF电纺纤维膜插层增强碳纤维/环氧树脂复合材料层间韧性[J]. 复合材料科学与工程, 2024, 0(4): 26-32.
[4]	武顺心, 朱水文. 基于改进的Halpin-Tsai模型对颗粒增强复合材料弹性常数预测[J]. 复合材料科学与工程, 2024, 0(4): 33-39.
[5]	李红军, 韩杨, 宋笑非, 郑绍文, 郑超凡, 孙九霄. 孔柱锥度对纤维柱增强夹芯结构压缩性能的影响[J]. 复合材料科学与工程, 2024, 0(4): 40-48.
[6]	刘冠三, 孙士勇, 马鑫, 韩晓缠. 基于激光加热的CF/PEEK复合材料层合板铺放工艺研究[J]. 复合材料科学与工程, 2024, 0(4): 49-55.
[7]	刘峰, 乔宇, 李雪江, 豆广征. 轻木夹芯/碳纤维复合材料结构后推构型无人机机身设计与分析[J]. 复合材料科学与工程, 2024, 0(4): 56-62.
[8]	田潇, 文立伟, 邓朱海. 缝合增强PRSEUS构件低速冲击性能研究[J]. 复合材料科学与工程, 2024, 0(4): 63-75.
[9]	梁桂龙, 丛庆, 李旭, 王继辉. 混杂纤维复合材料螺旋桨的铺层结构设计与模压成型工艺[J]. 复合材料科学与工程, 2024, 0(4): 83-89.
[10]	张恒, 方海, 王肖淳, 夏国龙, 徐双. 小角度缠绕复合材料护岸管桩抗弯性能试验与设计[J]. 复合材料科学与工程, 2024, 0(4): 90-96.
[11]	桂林景, 张世广, 李皓, 王安康, 梁鑫河, 夏岩峰, 刘佳. 复合材料过盈铆接结构吸湿老化行为研究[J]. 复合材料科学与工程, 2024, 0(4): 97-104.
[12]	王浩东, 侯增选, 张伟超, 罗洋洋, 李彦良, 戚厚良. 基于蚁群算法的绝热层缠绕路径优化[J]. 复合材料科学与工程, 2024, 0(4): 105-110.
[13]	周欣康, 位浩杰, 陈晓龙, 王佳鑫, 卢大伟, 谢辉. 刀具磨损因素分析及对CFRP制孔质量的影响[J]. 复合材料科学与工程, 2024, 0(4): 111-116.
[14]	盛洁, 刘航, 王文乐, 姜生坤, 李明霞, 黄正强, 耿铁, 蒋林. 多刺激响应型高强度复合材料柔性致动器研究进展[J]. 复合材料科学与工程, 2024, 0(4): 117-128.
[15]	王孟, 刘程, 张玉, 贾航, 乔越, 蹇锡高. 成型温度对CF/PPEK复合材料的缺陷和力学性能影响[J]. 复合材料科学与工程, 2024, 0(3): 5-12.