增强聚氨酯硬质泡沫塑料压缩性能研究

摘要/Abstract

摘要：

利用中空玻璃微珠和纳米二氧化硅作为增强剂,制备了增强聚氨酯硬质泡沫塑料(RPURF),对其压缩性能进行了研究,并在金相显微镜下观察了它的微观结构。实验结果表明,泡孔支柱处的增强剂加强了其承载能力,有利于压缩性能的提高；随着增强剂用量的增加,PURF压缩强度和模量先增加后降低,即增强剂用量处于最佳用量范围内时,PURF体现最好的压缩性能；并随着纯聚氨酯硬质泡沫塑料密度的增加,其压缩性能有显著的提高。

关键词: 中空玻璃微珠, 纳米二氧化硅, 硬质聚氨酯泡沫塑料, 压缩性能

Abstract:

The polyurethane rigid foam (PURF) reinforced by nanometer silicon dioxide and hollow glass beads are prepared by highspeed mechanical agitation method,the compress mechanical properties of filledtype PURF are studied.Meanwhile,The distributed pattern of PURF particles is observed by microscope．The results show that the bearing capacity of cellular columniation is evidently improved by the infilling of additive.With the increasing content of additive,the compress strength of PURF was effectively enhanced first and decreased later,namely,the compress mechanic properties of the composites are the highest when the amount of additive is the best dosage；and with the improving density of PURF,the compress properties of the composites are evidently enhanced.

中图分类号:

TQ328.3

夏凡, 吴晓青. 增强聚氨酯硬质泡沫塑料压缩性能研究[J]. 玻璃钢/复合材料, 2009, 209(3): 53-55.

XIA Fan, WU Xiao-Qing. STUDY ON COMPRESS MECHANICAL PROPERTIES OF
REINFORCED POLYURETHANE RIGID FOAM[J]. Fiber Reinforced Plastics/Composites, 2009, 209(3): 53-55.

参考文献

［1］赵鹏飞,张元明,何颖等.玻璃钢蒙皮/聚氨酯泡沫塑料夹芯结构无人机机翼制造（一）工艺方案设计［J］.玻璃钢/复合材料,2001,(3):2931.
［2］赵鹏飞,张元明,何颖等.玻璃钢蒙皮/聚氨酯泡沫塑料夹芯结构无人机机翼制造（二）制造工艺过程［J］.玻璃钢/复合材料,2001,(2) :3739.
［3］孙春方,李文晓,薛元德等.高速列车用PMI泡沫力学性能研究［J］.玻璃钢/复合材料，2006,(4): 1319.
［4］韦生文.A型夹芯复合材料在地面雷达天线罩中的应用［J］.纤维复合材料，2005,19(2): 1926.
［5］李兴翼.复合材料柱/泡沫夹芯结构板成型工艺及性能研究［D］.哈尔滨：哈尔滨工业大学,2006.
［6］王章忠,沈志良.聚氨酯硬泡芯材夹层结构的开发与应用［J］.化学建材，2002,(4):2123.
［7］赵斌,杨振国,王建华等.增强聚氨酯硬泡塑料压缩性能的研究与表征［J］.纤维复合材料，2003,3(3): 35.
［8］闻荻江,陈再新.增强泡沫塑料的特性和应用［J］.玻璃钢/复合材料,1998,(2): 4951.
［9］王建华,芦艾,周秋明等.短切玻璃纤维增强硬质聚氨酯泡沫塑料的压缩性能［J］.高分子材料科学与工程,2001,17(3):150.
［10］王伟力,徐标.RPU力学性能与密度和增强相含量的关系［J］.化工生产与技术,2001,8(5):1012.
［11］张慧波,杨绪杰.陶瓷微珠填充聚氨酯弹性体复合材料性能研究［J］.玻璃钢/复合材料，2007,(1):2427.
［12］周秋明,王建华.空心玻璃微珠复合聚氨酯泡沫塑料的泡孔结构与性能［J］.聚氨酯工业,2002,2(17):1315.
［13］耿皓.纳米颗粒对包装材料硬质聚氨酯泡沫塑料力学性能的影响［J］.包装工程,2006,27(4):5052.
［14］陈小金,陈宪宏.聚氨酯/纳米复合材料的研究进展［J］.材料科学与工程学报,2005,23(6):929932.
［15］马继盛,漆宗能.聚氨酯弹性体/蒙脱土纳米复合材料的合成、结构与性能［J］.高分子学报,2001,(3):325328.
［16］张琼方,张教强,国际英.纳米粒子增韧聚氯乙烯研究新进展［J］.玻璃钢/复合材料,2005,(1): 5356.
［17］顾军渭,吕丽.UPR/纳米SiO2复合材料的制备［J］.纤维复合材料,2005,(3): 1114.
［18］ Chalivendar.V.B.Processing and Mechanical Characterization of Lightweight Polyurethane Composites［J］.Journal of Materials Science,2003,38(8):16311643.
［19］ Puterman.M.,Narkis.M.Syntactic foams I: Preparation Structure and Properties［J］.Journal of Cellular Plastics,1980,16(4):223229.
［20］ Parameswaran.V.,Shukla.A.Processing and Characterization of a Model Functionally Gradient Materia［J］.Journal of Materials Science,2000,35(1): 2129.

[1]	李成金, 李静, 夏锦红. 玄武岩-PVA纤维协同增强轻骨料混凝土抗弯拉及抗冲击性能[J]. 复合材料科学与工程, 2022, 0(6): 70-75.
[2]	苏雨茹, 关志东, 王鑫, 张书铭, 黎增山. 挖补修理复合材料层合板静力压缩与疲劳性能试验研究[J]. 复合材料科学与工程, 2021, 0(5): 98-103.
[3]	张甲瑞, 翟光涛. 基于空间编织法制备的连续纤维复合点阵材料及其压缩性能研究[J]. 复合材料科学与工程, 2021, 0(3): 45-50.
[4]	魏建国, 李帅旗, 马端人, 柳佳. 成型工艺对聚氨酯合成轨枕性能影响的研究[J]. 复合材料科学与工程, 2020, 0(11): 111-115.
[5]	郑国栋, 徐晓明, 雷娟娟, 张晶. 海水对PMI泡沫夹芯复合材料吸湿性能以及力学性能的影响[J]. 玻璃钢/复合材料, 2019, 0(9): 105-109.
[6]	刘明帆, 张鹏, 程永奇. 二维多轴向经编碳纤维复合材料性能研究[J]. 玻璃钢/复合材料, 2019, 0(7): 28-33.
[7]	叶梯, 岳源. 复合材料长桁压缩性能数值分析及试验验证[J]. 玻璃钢/复合材料, 2019, 0(7): 34-38.
[8]	杨龙英. 不同缝合方式对缝合复合材料力学性能的影响研究[J]. 玻璃钢/复合材料, 2018, 0(6): 99-103.
[9]	周振方, 王立和, 葛平, 彭周岗. SMC轻量化初步探究[J]. 玻璃钢/复合材料, 2018, 0(4): 92-97.
[10]	冯古雨, 曹海建, 周红涛, 卢雪峰. 三维机织复合材料单胞模型各向异性的有限元分析[J]. 玻璃钢/复合材料, 2017, 0(8): 48-52.
[11]	刘强, 陈航. EPP泡沫填充对铝蜂窝压缩性能的影响研究[J]. 玻璃钢/复合材料, 2017, 0(3): 49-52.
[12]	檀江涛,马晓红,秦志刚. 二维编织复合材料管件轴向压缩性能研究[J]. 玻璃钢/复合材料, 2017, 0(12): 57-59.
[13]	付成龙,陈利,张雅璐. 几何尺寸与温度对CFRP筋材力学性能的影响[J]. 玻璃钢/复合材料, 2016, 0(5): 74-79.
[14]	李克迪,方勇,胡爱军,徐时彧. 储存期对聚甲基丙烯酰亚胺(PMI)泡沫性能的影响研究[J]. 玻璃钢/复合材料, 2016, 0(3): 70-74.
[15]	严文聪, 曾金芳, 李朝阳, 雷涛. 芳纶Ⅲ纤维及其混杂碳纤维复合材料的压缩性能研究[J]. 玻璃钢/复合材料, 2016, 0(11): 90-93.